Capacitive humidity sensors based on large diameter porous alumina prepared by high current anodization

Abstract Humidity sensors based on nanoporous aluminum oxide are described. Accelerated mild anodization technique was employed to prepare ordered porous aluminum oxide templates in phosphoric acid electrolyte at 165 and 185 V, anodization voltages. Impedance spectroscopy was used to characterize sensitivity, response and recovery time of prepared sensors with pore diameters changing from 67 to 190 nm. Increasing the pores diameter to an optimum limit improved the sensing parameters of the prepared sensors. Sensitivity enhancement was accompanied with reduction of humidity sensing threshold to 30% RH at optimum condition. Their low response and recovery time, less than 5 and 0.5 s, respectively, categorize them as ultrafast or rapid sensors. Sensing properties is seen to reduce with reduce in aluminum purity while it improves with increase in the self ordering of alumina template. It is also found that increasing the anions percentage in the pores walls improves the sensing behavior.

[1]  Hyunchul Park,et al.  Capacitive humidity sensor design based on anodic aluminum oxide , 2009 .

[2]  P. T. Lai,et al.  TECHNICAL NOTE: Moisture sensitive field effect transistors using ? gate structure , 1999 .

[3]  Noboru Yamazoe,et al.  Humidity sensors: Principles and applications , 1986 .

[4]  A. Ramazani,et al.  Self-Ordered Nanopore Arrays with 300–400 nm Interpore Distances Formed by High Field Accelerated Mild Anodization , 2011 .

[5]  M. Brett,et al.  Impact of morphology on high-speed humidity sensor performance , 2006, IEEE Sensors Journal.

[6]  Enrico Traversa,et al.  Ceramic sensors for humidity detection: the state-of-the-art and future developments , 1995 .

[7]  Reinald Hillebrand,et al.  Perfect two-dimensional porous alumina photonic crystals with duplex oxide layers , 2003 .

[8]  Kenji Fukuda,et al.  Ordered Metal Nanohole Arrays Made by a Two-Step Replication of Honeycomb Structures of Anodic Alumina , 1995, Science.

[9]  W. Shen,et al.  High-performance humidity sensors based on high-field anodized porous alumina films , 2009, Nanotechnology.

[10]  Debdulal Saha,et al.  Dependence of moisture absorption property on sol-gel process of transparent nano-structured γ-Al2O3 ceramics , 2005 .

[11]  Vinod Kumar Khanna,et al.  Carrier-transfer mechanisms and Al2O3 sensors for low and high humidities , 1986 .

[12]  K. Wada,et al.  Fabrication of Ideally Ordered Nanoporous Alumina Films and Integrated Alumina Nanotubule Arrays by High‐Field Anodization , 2005 .

[13]  A. C. Jason,et al.  Effects of Water Vapour on the Electrical Properties of Anodized Aluminium , 1953, Nature.

[14]  Vincent K. S. Hsiao,et al.  Humidity sensing based on nanoporous polymeric photonic crystals , 2008 .

[15]  H. Grange,et al.  A capacitive humidity sensor with every fast response time and very low hysteresis , 1987 .

[16]  Antoni Nowakowski,et al.  Preparation and properties of nanoporous alumina-based humidity sensors , 2006, Optoelectronic and Electronic Sensors.

[17]  Craig A. Grimes,et al.  Room Temperature Ammonia and Humidity Sensing Using Highly Ordered Nanoporous Alumina Films , 2002 .

[18]  Jean-Paul Randin,et al.  Relative humidity measurement using a coated piezoelectric quartz crystal sensor , 1987 .