Numerical surface characterization of wear debris from artificial joints using atomic force microscopy

Study on surface features of wear particles generated in wear process provides an insight into the progress of material failure of artificial joints. It is very important to quantify the surface features of wear particles in three dimensions. In this study, a new approach using atomic force microscopy was proposed to carry out 3D numerical surface characterization of wear debris generated from artificial joints. Atomic force microscopy combined with image processing techniques was used to acquire appropriate 3D images of wear debris. Computerized image analysis techniques were then used to quantify surface texture features of wear debris such as surface roughness parameters and surface texture index. The method developed from the present study was found to be feasible to quantity the surface characterization of nano- and micro-sized wear debris generated from artificial joints.

[1]  J. Fisher,et al.  Isolation and characterization of UHMWPE wear particles down to ten nanometers in size from in vitro hip and knee joint simulators. , 2006, Journal of biomedical materials research. Part A.

[2]  A. Sosna,et al.  Nanometer size wear debris generated from ultra high molecular weight polyethylene in vivo , 2009 .

[3]  J. Williams,et al.  Wear debris and associated wear phenomena—fundamental research and practice , 2000 .

[4]  M. Morrison,et al.  Particle analysis for the determination of UHMWPE wear. , 2005, Journal of biomedical materials research. Part B, Applied biomaterials.

[5]  Z. Shao,et al.  Biological atomic force microscopy: what is achieved and what is needed , 1996 .

[6]  Xinping Yan,et al.  The surface roughness evolutions of wear particles and wear components under lubricated rolling wear condition , 2005 .

[7]  C. Kowandy,et al.  Isolation and analysis of articular joints wear debris generated in vitro , 2006 .

[8]  Pawel Podsiadlo,et al.  3-D imaging of surface topography of wear particles found in synovial joints , 1999 .

[9]  B. Wroblewski,et al.  Quantitative analysis of polyethylene wear debris, wear rate and head damage in retrieved Charnley hip prostheses , 2000, Journal of materials science. Materials in medicine.

[10]  Paul W. Michael,et al.  Atomic Force Microscopy of Geroler Motor Wear Debris Ferrograms , 2009 .

[11]  Jianhua Zhang,et al.  A bionic artificial joint system and investigation of tribological performance , 2009 .

[12]  J. Fisher,et al.  Nanometre size wear debris generated from crosslinked and non-crosslinked ultra high molecular weight polyethylene in artificial joints , 2005 .

[13]  Pawel Podsiadlo,et al.  Surface characterization of wear particles , 1999 .

[14]  D. Dowson.  History of Tribology , 1979 .

[15]  Mervyn J Miles,et al.  A mechanical microscope: High speed atomic force microscopy , 2005 .

[16]  Liao Qianchu.  Principle and prospect to improve the resolution of field emission scanning electron microscope , 2000 .

[17]  G. Stachowiak,et al.  The Application of the Modified Partitioned Iterated Function System (PIFS) to the Characterization and Classification of Wear Particles and Surfaces , 2001 .