A biomimetic tubular scaffold with spatially designed nanofibers of protein/PDS® bio‐blends

Electrospun tubular conduit (4 mm inner diameter) based on blends of polydioxanone (PDS II®) and proteins such as gelatin and elastin having a spatially designed trilayer structure was prepared for arterial scaffolds. SEM analysis of scaffolds showed random nanofibrous morphology and well‐interconnected pore network. Due to protein blending, the fiber diameter was reduced from 800–950 nm range to 300–500 nm range. Fourier‐transform infrared spectroscopy (FTIR) and differential scanning calorimetry (DSC) results confirmed the blended composition and crystallinity of fibers. Pure PDS scaffold under hydrated state exhibited a tensile strength of 5.61 ± 0.42 MPa and a modulus of 17.11 ± 1.13 MPa with a failure strain of 216.7 ± 13%. The blending of PDS with elastin and gelatin has decreased the tensile properties. A trilayer tubular scaffold was fabricated by sequential electrospinning of blends of elastin/gelatin, PDS/elastin/gelatin, and PDS/gelatin (EG/PEG/PG) to mimic the complex matrix structure of native arteries. Under hydrated state, the trilayer conduit exhibited tensile properties (tensile strength of 1.77 ± 0.2 MPa and elastic modulus of 5.74 ± 3 MPa with a failure strain of 75.08 ± 10%) comparable to those of native arteries. In vitro degradation studies for up to 30 days showed about 40% mass loss and increase in crystallinity due to the removal of proteins and “cleavage‐induced crystallization” of PDS. Biotechnol. Bioeng. 2009; 104: 1025–1033. © 2009 Wiley Periodicals, Inc.

[1]  A. Müller,et al.  Crystallisation and morphology of poly(p‐dioxanone) , 2000 .

[2]  T. V. How,et al.  Mechanical Properties of Arteries and Arterial Grafts , 1992 .

[3]  C. Chu,et al.  Hydrolytic degradation and morphologic study of poly-p-dioxanone. , 1993, Journal of biomedical materials research.

[4]  Yi Hong,et al.  Fabrication of cell microintegrated blood vessel constructs through electrohydrodynamic atomization. , 2007, Biomaterials.

[5]  R. Cameron,et al.  The hydrolytic degradation of polydioxanone (PDSII) sutures. Part I: Morphological aspects. , 2002, Journal of biomedical materials research.

[6]  P. Degée,et al.  Hydrolytic Degradation of Double Crystalline PPDX‐b‐PCL Diblock Copolymers , 2005 .

[7]  David G Simpson,et al.  Electrospinning collagen and elastin: preliminary vascular tissue engineering. , 2004, Frontiers in bioscience : a journal and virtual library.

[8]  Xiu-li Wang,et al.  In vitro degradation of biodegradable blending materials based on poly(p-dioxanone) and poly(vinyl alcohol)-graft-poly(p-dioxanone) with high molecular weights. , 2007, Journal of biomedical materials research. Part A.

[9]  A. R. Santos,et al.  Blends of poly(3-hydroxybutyrate) and poly(p-dioxanone): miscibility, thermal stability and biocompatibility , 2008, Journal of materials science. Materials in medicine.

[10]  M. Zilberman.  Dexamethasone loaded bioresorbable films used in medical support devices: structure, degradation, crystallinity and drug release. , 2005, Acta biomaterialia.

[11]  S. Ramakrishna,et al.  Fabrication of modified and functionalized polycaprolactone nanofibre scaffolds for vascular tissue engineering , 2005, Nanotechnology.

[12]  Anthony Atala,et al.  In vitro evaluation of electrospun nanofiber scaffolds for vascular graft application. , 2007, Journal of biomedical materials research. Part A.

[13]  S. Agarwal,et al.  Use of electrospinning technique for biomedical applications , 2008 .

[14]  S. Ramakrishna,et al.  Fabrication and endothelialization of collagen-blended biodegradable polymer nanofibers: potential vascular graft for blood vessel tissue engineering. , 2005, Tissue engineering.

[15]  Xing Zhang,et al.  In vitro biodegradation of designed tubular scaffolds of electrospun protein/polyglyconate blend fibers. , 2009, Journal of biomedical materials research. Part B, Applied biomaterials.

[16]  G. Bowlin,et al.  Extracellular matrix regenerated : tissue engineering via electrospun biomimetic nanofibers , 2007 .

[17]  Y. Tabata,et al.  Fabrication and biocompatibility of collagen sponge reinforced with poly(glycolic acid) fiber. , 2003, Tissue engineering.

[18]  Seeram Ramakrishna,et al.  Electrospinning of gelatin fibers and gelatin/PCL composite fibrous scaffolds. , 2005, Journal of biomedical materials research. Part B, Applied biomaterials.

[19]  A. Müller,et al.  Influence of in vitro hydrolytic degradation on the morphology and crystallization behavior of poly(p-dioxanone). , 2004, Biomacromolecules.

[20]  Jack G. Zhou,et al.  Structure and morphology changes in absorbable poly(glycolide) and poly(glycolide-co-lactide) during in vitro degradation , 1999 .

[21]  Katja Schenke-Layland,et al.  Three-dimensional electrospun ECM-based hybrid scaffolds for cardiovascular tissue engineering. , 2008, Biomaterials.

[22]  Dan T Simionescu,et al.  In vivo cellular repopulation of tubular elastin scaffolds mediated by basic fibroblast growth factor. , 2007, Biomaterials.

[23]  E. Duek,et al.  Hydrolytic degradation of poly(para-dioxanone) films prepared by casting or phase separation , 2002 .

[24]  D. C. Knapp,et al.  Electrospun polydioxanone–elastin blends: potential for bioresorbable vascular grafts , 2006, Biomedical materials.

[25]  G. Bowlin,et al.  Cross-linking Electrospun Polydioxanone-Soluble Elastin Blends: Material Characterization , 2008 .

[26]  Anthony Atala,et al.  Controlled fabrication of a biological vascular substitute. , 2006, Biomaterials.

[27]  Horst A von Recum,et al.  Electrospinning: applications in drug delivery and tissue engineering. , 2008, Biomaterials.

[28]  Anthony Atala,et al.  The in vivo stability of electrospun polycaprolactone-collagen scaffolds in vascular reconstruction. , 2009, Biomaterials.

[29]  David G Simpson,et al.  Electrospinning polydioxanone for biomedical applications. , 2005, Acta biomaterialia.

[30]  Derrick Dean,et al.  Nanostructured Biomaterials for Regenerative Medicine , 2006 .

[31]  J. Im,et al.  In vitro and in vivo degradation behaviors of synthetic absorbable bicomponent monofilament suture prepared with poly(p-dioxanone) and its copolymer , 2007 .

[32]  X. Mo,et al.  Electrospinning P(LLA-CL) nanofiber: A tubular scaffold fabrication with circumferential alignment , 2004 .

[33]  Jonathan Bard,et al.  COLLAGEN SUBSTRATA FOR STUDIES ON CELL BEHAVIOR , 1972, The Journal of cell biology.

[34]  Takehisa Matsuda,et al.  Mesoscopic spatial designs of nano- and microfiber meshes for tissue-engineering matrix and scaffold based on newly devised multilayering and mixing electrospinning techniques. , 2005, Biomaterials.

[35]  Xing Zhang,et al.  Functionally graded electrospun scaffolds with tunable mechanical properties for vascular tissue regeneration , 2007, Biomedical materials.

[36]  Xuesi Chen,et al.  Co-electrospun poly(lactide-co-glycolide), gelatin, and elastin blends for tissue engineering scaffolds. , 2006, Journal of biomedical materials research. Part A.