A new compounding method for exfoliated graphite–polypropylene nanocomposites with enhanced flexural properties and lower percolation threshold

Nanocomposites made of polypropylene reinforced with exfoliated graphite nanoplatelets (xGnP™), are fabricated by melt mixing, polymer solution and coating. Coating is a new compounding method proposed in this research, where xGnP and PP powder are premixed in isopropyl alcohol using sonication to disperse the xGnP by coating individual PP powder particles. It is found that the coating method is more effective than the polymer solution method widely used, in terms of lowering the percolation threshold of thermoplastic nanocomposites, and enhancing the probability that the large platelet morphology of xGnP can be preserved in the final composite. The research reported here provides an understanding on how the compounding method used during the fabrication of nanocomposites is important to achieving the optimal flexural properties, electrical conductivity and percolation threshold. This method should have wide applicability to all thermoplastic matrix nanocomposite systems.

[1]  Wengui Weng,et al.  HDPE/expanded graphite electrically conducting composite , 2004 .

[2]  Guohua Chen,et al.  Preparation of polymer/graphite conducting nanocomposite by intercalation polymerization , 2001 .

[3]  I. Krupa,et al.  “Percolation effect” and mechanical behavior of carbon black filled polyethylene , 1999 .

[4]  J. T. Lindt,et al.  Electrical properties of exfoliated‐graphite filled polyethylene composites , 1986 .

[5]  Igor Krupa,et al.  Physical properties of thermoplastic/graphite composites , 2001 .

[6]  D. Kalyon,et al.  Effects of particle shape and size distributions on the electrical and magnetic properties of nickel/polyethylene composites , 1993 .

[7]  D. Bigg.  The effect of compounding on the conductive properties of EMI shielding compounds , 1984 .

[8]  L. Lan,et al.  The effect of particle size on electric conducting percolation threshold in polymer/conducting particle composites , 2000 .

[9]  Alain Celzard,et al.  Composites based on micron-sized exfoliated graphite particles: Electrical conduction, critical exponents and anisotropy , 1996 .

[10]  Guo-Hua Hu,et al.  A new process of fabricating electrically conducting nylon 6/graphite nanocomposites via intercalation polymerization , 2000 .

[11]  M. Xiao,et al.  Synthesis and characterization of polyaniline/graphite conducting nanocomposites , 2004 .

[12]  D. Kalyon,et al.  Percolation in magnetic composites , 1997 .

[13]  W. Huang,et al.  Structure and electrical properties of grafted polypropylene/graphite nanocomposites prepared by solution intercalation , 2003 .

[14]  Shing Chung Josh Wong,et al.  Electrical conductivity and dielectric properties of PMMA/expanded graphite composites , 2003 .

[15]  B. Mandal,et al.  Conducting polyaniline nanoparticle blends with extremely low percolation thresholds , 1995 .

[16]  Mária Omastová,et al.  Relation between electrical and mechanical properties of conducting polymer composites , 2001 .

[17]  Julia A. King,et al.  Evaluation of electrical conductivity models for conductive polymer composites , 2002 .

[18]  Wengui Weng,et al.  Preparation of polystyrene–graphite conducting nanocomposites via intercalation polymerization , 2001 .

[19]  Min Xiao,et al.  Preparation of exfoliated graphite/polystyrene composite by polymerization-filling technique , 2001 .

[20]  Z. Yu,et al.  Conductive mechanism of polymer/graphite conducting composites with low percolation threshold , 2002 .

[21]  S. Wong,et al.  Electrical and mechanical properties of expanded graphite‐reinforced high‐density polyethylene , 2004 .

[22]  S. Wong,et al.  TRANSPORT BEHAVIOR OF PMMA/EXPANDED GRAPHITE NANOCOMPOSITES , 2002 .