Prediction of impact-induced delamination in cross-ply composite laminates using cohesive interface elements

Abstract The paper investigates the potential of cohesive interface elements for damage prediction in laminates subjected to low-velocity impact. FE models with interface elements adopting a bilinear cohesive law were first calibrated and validated by simulation of standard fracture toughness tests and then employed to model the impact response of cross-ply graphite/epoxy laminated plates. The developed model provided a correct simulation of the impact response of laminates in a wide range of energy values and successfully predicted size, shape and location of main damage mechanisms. The results of the analyses also pointed out the importance of employing a damage criterion capable of accounting for the constraining effect of out-of-plane compression on the initiation of the decohesion phase.

[1]  M. Crisfield,et al.  Finite element interface models for the delamination analysis of laminated composites: mechanical and computational issues , 2001 .

[2]  Pedro P. Camanho,et al.  An engineering solution for mesh size effects in the simulation of delamination using cohesive zone models , 2007 .

[3]  Larsgunnar Nilsson,et al.  Simulation of low velocity impact on fiber laminates using a cohesive zone based delamination model , 2004 .

[4]  ScienceDirect.  Composites. Part A, Applied science and manufacturing , 1996 .

[5]  P. Priolo,et al.  Damage response of stitched cross-ply laminates under impact loadings , 2007 .

[6]  M.F.S.F. de Moura,et al.  Modelling the interaction between matrix cracking and delamination in carbon–epoxy laminates under low velocity impact , 2004 .

[7]  M. Richardson,et al.  The finite element analysis of impact induced delamination in composite materials using a novel interface element , 1998 .

[8]  Ronald Krueger,et al.  The Virtual Crack Closure Technique : History , Approach and Applications , 2002 .

[9]  Larsgunnar Nilsson,et al.  Modeling of delamination using a discretized cohesive zone and damage formulation , 2002 .

[10]  J. Reeder,et al.  An Evaluation of Mixed-Mode Delamination Failure Criteria , 1992 .

[11]  Tong Earn Tay,et al.  Characterization and analysis of delamination fracture in composites: An overview of developments from 1990 to 2001 , 2003 .

[12]  Alberto Corigliano,et al.  Simulation of damage in composites by means of interface models: parameter identification , 2001 .

[13]  Ping Zhu,et al.  Finite element analysis of low-velocity impact damage in composite laminated plates , 2006 .

[14]  M. A. Crisfield,et al.  Progressive Delamination Using Interface Elements , 1998 .

[15]  P. Camanho,et al.  Numerical Simulation of Mixed-Mode Progressive Delamination in Composite Materials , 2003 .

[16]  P. Geubelle,et al.  Impact-induced delamination of composites: A 2D simulation , 1998 .

[17]  Nobuo Takeda,et al.  Numerical simulation of interlaminar damage propagation in CFRP cross-ply laminates under transverse loading , 2007 .

[18]  C. Ruiz,et al.  A delamination criterion for laminated composites under low-velocity impact , 2001 .

[19]  Stephen R Reid,et al.  A continuum damage model for delaminations in laminated composites , 2003 .

[20]  Wing Kam Liu,et al.  Nonlinear Finite Elements for Continua and Structures , 2000 .