论文信息 - Preparation of YBCO Superconducting Films by Sol-Gel Process

Preparation of YBCO Superconducting Films by Sol-Gel Process

precursor solution was prepared using barium trifluoroacetae (Ba-TFA) and non-fluorine yttrium (Y) and copper (Cu) organic salts. The precursor solution was modified by benzalacetone (BzAcH), in which the Cu2+ were chelated with BzAcH, which preventing the loss of Cu in the pyrolysis process. Dense YBCO superconducting films with smooth surface, which confirmed by scanning electron microscopy (SEM), were repeatedly obtained through sol-gel process. X-ray diffraction (XRD) 2θ scanning and φ scanning indicated that the as-prepared YBCO films had good c-axis texture. YBCO films with superconducting transition temperature (TC) above 89K were obtained.

R. Xue | L. Lei | G. Zhao | Y. Chen | Huangli Zhang

[1] J. Xiong,et al. Effect of annealing time on the structure and properties of YBCO films by the TFA-MOD method , 2005 .

[2] Y. Shiohara,et al. Numerical simulation of TFA-MOD process , 2005 .

[3] Y. Shiohara,et al. Fabrication of YBCO coated conductors using advanced TFA-MOD process , 2005 .

[4] Y. Xu,et al. High performance YBCO films by the hybrid of non-fluorine yttrium and copper salts with Ba–TFA , 2005 .

[5] T. Saitoh,et al. Advanced TFA-MOD process of high critical current YBCO films for coated conductors , 2004 .

[6] M. Cima,et al. Reactions of oxyfluoride precursors for the preparation of barium yttrium cuprate films , 2004 .

[7] I. Hirabayashi,et al. Microstructural observation of YBa2Cu3O7-xthin films prepared by TFA-MOD method , 2003 .

[8] Y. Sun,et al. Preparation of YBa2Cu3O7−δ films by MOD method using trifluoroacetate as precursor , 2003 .

[9] Y. Ikuhara,et al. Growth mechanism of Y123 film by MOD-TFA process , 2002 .

[10] Kazumi Kato,et al. Growth model and the effect of CuO nanocrystallites on the properties of chemically derived epitaxial thin films of YBa2Cu3O7−x , 2002 .