Effects of a laser surface processing induced heat-affected zone on the fatigue behavior of AISI 4340 steel

The effects of the heat-affected zone (HAZ) in AISI 4340 steel created by laser-surface alloying (LSA) on high-cycle fatigue behavior have been investigated. This research was performed by producing several lots of laser-processed AISI 4340 steel using different laser processing parameters, and then subjecting the samples to high-cycle fatigue and Knoop microindentation hardness studies. Samples of tested material from each lot were examined using scanning-electron microscopy (SEM) in order to establish the effects of laser processing on the microstructure of the fatigue-tested AISI 4340 steel. When these three techniques, microindentation hardness testing, high-cycle fatigue testing, and SEM, are combined, a mechanistic understanding of the effect of the HAZ on the fatigue behavior of this alloy might be gained. It was found that the HAZ did not appear to have an adverse effect on the high-cycle fatigue behavior of LSA-processed AISI 4340 steel.

[1]  P. Dearnley,et al.  Magnetron sputter deposition of chromium diboride coatings , 1998 .

[2]  P. Liaw,et al.  Fatigue crack growth behavior of 4340 steels , 1987 .

[3]  P. Liaw,et al.  Influence of oxide-induced crack closure on near-threshold fatigue crack growth behavior , 1982 .

[4]  R. Shiue,et al.  Laser transformation hardening of tempered 4340 steel , 1992 .

[5]  N. Dahotre,et al.  Development of microstructure in laser surface alloying of steel with chromium , 1990 .

[6]  Peter K. Liaw,et al.  Fracture behavior of 63sn-37pb solder , 1990 .

[7]  N. Dahotre,et al.  Synthesis of Boride Coating on Steel using High Energy Density Processes: Comparative Study of Evolution of Microstructure , 1999 .

[8]  R. S. Williams,et al.  Near-threshold fatigue crack growth behavior in copper , 1982 .

[9]  K. S. Kim,et al.  Fracture resistance of a steel weld joint under fatigue loading , 2000 .

[10]  Peter K. Liaw,et al.  Near-threshold fatigue crack growth behavior in metals , 1983 .

[11]  D. Y. Lee,et al.  In situ fracture observations on tempered martensite embrittlement in an AlSl 4340 steel , 1991 .

[12]  J. Doong,et al.  Fatigue Crack Growth in Laser Weldments of a Cold Rolled Steel , 1996 .

[13]  K. Peng,et al.  Effect of second phase on the fatigue crack growth in AlSl 4340 steel , 1996 .

[14]  L. W. Tsay,et al.  Fatigue crack propagation of D6AC laser welds , 1997 .

[15]  Peter K. Liaw,et al.  Tensile, fracture toughness and fatigue crack growth rate properties of silicon carbide whisker and particulate reinforced aluminum metal matrix composites , 1986 .

[16]  J. Zahavi,et al.  Laser alloying and cladding for improving surface properties , 1996 .

[17]  J. Onõro,et al.  Fatigue behaviour of laser welds of high-strength low-alloy steels , 1997 .