Crack propagation trajectories for rocks under mixed mode I–II fracture

Abstract Propagation of a crack in engineering materials including rocks can cause failure. Knowledge of the stress state under which a crack can propagate, and the trajectory it may follow during its growth are thus very important for the stability of rock masses/materials and for the safe design of structures in/on rocks. In this paper, the crack initiation angle and subsequent crack propagation path are experimentally investigated for limestone rock specimens. This investigation was conducted under various mixed mode I–II loading conditions, including pure mode-I and pure mode-II. This study includes conducting diametrical compression tests on notched Brazilian disk specimens. Moreover, the effect of confining pressure and temperature on crack initiation and propagation were also studied. The experimental results were compared with theoretical predictions of crack initiation angle. The results showed that limestone behaves in brittle fashion, and the effects of confining pressure and temperature on failure trajectories were not significant. Generally, the crack initiation angle can be predicted by the maximum tangential stress criterion. However, for notched Brazilian disk with high value of crack orientation with respect to loading direction, crack does not propagate from the tip of the crack. This important observation indicated that the tensile-strength failure can become more critical than the fracture-toughness failure.

[1]  G. Papakaliatakis,et al.  Trajectories of unstably growing cracks in mixed mode I–II loading of marble beams , 1997 .

[2]  Jehuda Tirosh,et al.  Mixed-mode fracture angle and fracture locus of materials subjected to compressive loading , 1981 .

[3]  H. Awaji,et al.  Combined Mode Fracture Toughness Measurement by the Disk Test , 1978 .

[4]  Luis E. Vallejo.  The Brittle And Ductile Behavior Of A Material Containing A Crack Under Mixed-Mode Loading , 1987 .

[5]  N. A. Al-Shayea,et al.  Effect of Specimen Geometry and Testing Method on Mixed Mode I–II Fracture Toughness of a Limestone Rock from Saudi Arabia , 2000 .

[6]  Wang Sijing,et al.  AN EXPERIMENTAL INVESTIGATION CONCERNING THE COMPREHENSIVE FRACTURE TOUGHNESS OF SOME BRITTLE ROCKS , 1985 .

[7]  B. N. Whittaker,et al.  Rock fracture mechanics , 1992 .

[8]  F. Erdogan,et al.  On the Crack Extension in Plates Under Plane Loading and Transverse Shear , 1963 .

[9]  Chengcheng Xu,et al.  The use of the cracked Brazilian disc geometry for rock fracture investigations , 1994 .

[10]  B. N. Whittaker,et al.  Rock Fracture Mechanics: Principles, Design and Applications , 1992 .

[11]  Peter Matic,et al.  An experimental and computational investigation of crack growth initiation in three-point bend fracture specimens , 1995 .

[12]  R. W. Powers,et al.  Geology of the Arabian Peninsula; sedimentary geology of Saudi Arabia , 1966 .

[13]  Sahel N. Abduljauwad,et al.  Effects of confining pressure and temperature on mixed-mode (I–II) fracture toughness of a limestone rock , 2000 .

[14]  Ernian Pan,et al.  Fracture Mechanics Analysis of Cracked Discs of Anisotropic Rock Using the Boundary Element Method , 1998 .

[15]  L. Vallejo.  Fissure Parameters in Stiff Clays under Compression , 1989 .

[16]  Musharraf Zaman,et al.  Fracture toughness of a soft sandstone , 1998 .

[17]  M. Pustejovsky.  Fatigue crack propagation in titanium under general in-plane loading—II: Analysis , 1979 .

[18]  C. Atkinson,et al.  Combined mode fracture via the cracked Brazilian disk test , 1982, International Journal of Fracture.

[19]  Luis E. Vallejo,et al.  The influence of fissures in a stiff clay subjected to direct shear , 1987 .

[20]  A. R. Rosenfield,et al.  Mixed-Mode Fracture of Ceramics in Diametral Compression , 1986 .

[21]  Michael A. Pustejovsky,et al.  Fatigue crack propagation in titanium under general in-plane loading—I: Experiments , 1979 .