Template-based fluoroethylenepropylene piezoelectrets with tubular channels for transducer applications

We describe the concept, the fabrication, and the most relevant properties of a piezoelectric-polymer system: Two fluoroethylenepropylene (FEP) films with good electret properties are laminated around a specifically designed and prepared polytetrafluoroethylene (PTFE) template at 300 °C. After removing the PTFE template, a two-layer FEP film with open tubular channels is obtained. For electric charging, the two-layer FEP system is subjected to a high electric field. The resulting dielectric barrier discharges inside the tubular channels yield a ferroelectret with high piezoelectricity. d33 coefficients of up to 160 pC/N have already been achieved on the ferroelectret films. After charging at suitable elevated temperatures, the piezoelectricity is stable at temperatures of at least 130 °C. Advantages of the transducer films include ease of fabrication at laboratory or industrial scales, a wide range of possible geometrical and processing parameters, straightforward control of the uniformity of the polymer ...

[1]  Werner Wirges,et al.  Thermal and Temporal Stability of Ferroelectret Films Made from Cellular Polypropylene/Air Composites , 2006 .

[2]  Michael Wegener,et al.  Microstorms in cellular polymers: a route to soft piezoelectric transducer materials with engineered macroscopic dipoles. , 2005, Chemphyschem : a European journal of chemical physics and physical chemistry.

[3]  Werner Wirges,et al.  Piezoelectric Polyethylene Terephthalate (PETP) Foams – Specifically Designed and Prepared Ferroelectret Films , 2005 .

[4]  R. Gerhard-Multhaupt,et al.  Piezoelectrets from thermo-formed bubble structures of fluoropolymer-electret films , 2006, IEEE Transactions on Dielectrics and Electrical Insulation.

[5]  J. West,et al.  Stabilization of positive charge in fluorinated ethylene propylene copolymer , 1984 .

[6]  Siegfried Bauer,et al.  Dielectric barrier microdischarges: Mechanism for the charging of cellular piezoelectric polymers , 2002 .

[7]  Xiaoqing Zhang,et al.  Improvement of piezoelectric activity of cellular polymers using a double-expansion process , 2004 .

[8]  Graham Williams,et al.  Conference on Electrical Insulation and Dielectric Phenomena , 1982, IEEE Transactions on Electrical Insulation.

[9]  Werner Wirges,et al.  Barrier discharges in cellular polypropylene ferroelectrets : How do they influence the electromechanical properties? , 2007 .

[10]  X. Qiu,et al.  Spectroscopic study of dielectric barrier discharges in cellular polypropylene ferroelectrets , 2007 .

[11]  U. Kogelschatz Dielectric-Barrier Discharges: Their History, Discharge Physics, and Industrial Applications , 2003 .

[12]  Xiaoqing Zhang,et al.  Thermally stable fluorocarbon ferroelectrets with high piezoelectric coefficient , 2006 .

[13]  Axel Mellinger,et al.  Dielectric resonance spectroscopy: a versatile tool in the quest for better piezoelectric polymers , 2003 .

[14]  M. Wegener,et al.  Corona-induced partial discharges, internal charge separation and electromechanical transducer properties in cellular polymer films , 2002, Proceedings. 11th International Symposium on Electrets.

[15]  Gerhard M. Sessler,et al.  Electromechanical response of cellular electret films , 1999 .

[16]  Werner Wirges,et al.  Two-step inflation of cellular polypropylene films: void-thickness increase and enhanced electromechanical properties , 2004 .

[17]  Peng Fang,et al.  Cellular polyethylene-naphthalate ferroelectrets: Foaming in supercritical carbon dioxide, structural and electrical preparation, and resulting piezoelectricity , 2007 .

[18]  G. Sessler,et al.  Ferroelectrets: Soft Electroactive Foams for Transducers , 2004 .