ROLE OF SURFACE CHEMISTRY ON ELECTRIC DOUBLE LAYER CAPACITANCE OF CARBON MATERIALS

Abstract A large number of porous carbon materials with different properties in terms of porosity, surface chemistry and electrical conductivity, were prepared and systematically studied as electric double layer capacitors in aqueous medium with H2SO4 as electrolyte. The precursors used are an anthracite, general purpose carbon fibres and high performance carbon fibres, which were activated by KOH, NaOH, CO2 and steam at different conditions. Among all of them, an activated anthracite with a BET surface area close to 1500 m2/g, presents the best performance, reaching a value of 320 F/g, using a three-electrode system. The results obtained for all the samples, agree with the well-known relationship between capacitance and porosity, and show that the CO-type oxygen groups have a positive contribution to the capacitance. A very good correlation between the specific capacitance and this type of oxygen groups has been found.

[1]  Keiichi Okajima,et al.  Capacitance behavior of activated carbon fibers with oxygen-plasma treatment , 2005 .

[2]  D. Lozano‐Castelló,et al.  Characterization of pore distribution in activated carbon fibers by microbeam small angle X-ray scattering , 2002 .

[3]  Yong Jung Kim,et al.  Structural features necessary to obtain a high specific capacitance in electric double layer capacitors , 2004 .

[4]  Hang Shi,et al.  Studies of activated carbons used in double-layer capacitors , 1998 .

[5]  M. Yoshio,et al.  Improvement of Commercial Activated Carbon and Its Application in Electric Double Layer Capacitors , 2002 .

[6]  E. Frąckowiak,et al.  Electrochemical capacitors based on highly porous carbons prepared by KOH activation , 2004 .

[7]  Hsisheng Teng,et al.  Influence of oxygen treatment on electric double-layer capacitance of activated carbon fabrics , 2002 .

[8]  D. Cazorla-Amorós,et al.  About reactions occurring during chemical activation with hydroxides , 2004 .

[9]  Hang Shi,et al.  Activated carbons and double layer capacitance , 1996 .

[10]  H. Teng,et al.  Influence of surface oxides on the impedance behavior of carbon-based electrochemical capacitors , 2003 .

[11]  I. R. Hill,et al.  Performance of experimental carbon blacks in aqueous supercapacitors , 2005 .

[12]  D. Cazorla-Amorós,et al.  Characterization of Activated Carbon Fibers by CO 2 Adsorption , 1996 .

[13]  D. Cazorla-Amorós,et al.  Activation of coal tar pitch carbon fibres: Physical activation vs. chemical activation , 2004 .

[14]  Dolores Lozano-Castelló,et al.  Preparation of activated carbons from spanish anthracite. II. Activation by NaOH , 2001 .

[15]  M. Toyoda,et al.  Exfoliated carbon fibers as an electrode for electric double layer capacitors in a 1 mol/dm3 H2SO4 electrolyte , 2004 .

[16]  D. Cazorla-Amorós,et al.  Tpd and TPR characterization of carbonaceous supports and Pt/C catalysts , 1993 .

[17]  D. Cazorla-Amorós,et al.  Effect of the activating gas on tensile strength and pore structure of pitch-based carbon fibres , 1994 .

[18]  E. Frąckowiak,et al.  Erratum to “Electrochemical capacitors based on highly porous carbons prepared by KOH activation”: [Electrochim. Acta 49 (2004) 515–523] , 2004 .

[19]  J. Figueiredo,et al.  Modification of the surface chemistry of activated carbons , 1999 .

[20]  Seongyop Lim,et al.  KOH activation of carbon nanofibers , 2004 .

[21]  D. Cazorla-Amorós,et al.  CO2 As an Adsorptive To Characterize Carbon Molecular Sieves and Activated Carbons , 1998 .

[22]  E. Frąckowiak,et al.  Effect of pore size distribution of coal-based activated carbons on double layer capacitance , 2005 .

[23]  Hsisheng Teng,et al.  Performance of electric double-layer capacitors using carbons prepared from phenol–formaldehyde resins by KOH etching , 2001 .

[24]  D. Cazorla-Amorós,et al.  Further Advances in the Characterization of Microporous Carbons by Physical Adsorption of Gases (特集「炭素の表面と機能発現」) , 1998 .

[25]  Chi-Chang Hu,et al.  Effects of electrolytes and electrochemical pretreatments on the capacitive characteristics of activated carbon fabrics for supercapacitors , 2004 .

[26]  D. Lozano‐Castelló,et al.  Influence of pore structure and surface chemistry on electric double layer capacitance in non-aqueous electrolyte , 2003 .

[27]  A. Ōya,et al.  Electric Double Layer Capacitance of Mesoporous Activated Carbon Fiber , 2001 .

[28]  J. Vázquez,et al.  Carbon–ceramic composites from coal tar pitch and clays: application as electrocatalyst support , 2002 .