Passivation and Depassivation of Si – SiO2 Interfaces with Atomic Hydrogen

The influence of atomic hydrogen on the surface passivation of the Si―SiO 2 interface is investigated. Inductively coupled photoconductivity decay measurements indicate an increase in carrier recombination at the surfaces following atomic hydrogen exposure, as measured by an increase in the emitter saturation current density. These defects are not thermally stable and are removed by subsequent thermal treatments above 300°C in N 2 . Atomic hydrogen results in the passivation of a certain fraction of thermally stable interface defects. However, the fraction of defects passivated is always slightly lower than can be achieved by exposure to molecular hydrogen. A variation in a sample temperature during atomic H exposure in the range of 25―400°C does not have a significant impact on the passivation efficiency.

[1]  K. Weber,et al.  Defect generation at SiO2/Si interfaces by low pressure chemical vapor deposition of silicon nitride , 2006 .

[2]  A. Aberle,et al.  Optimization and characterization of remote plasma-enhanced chemical vapor deposition silicon nitride for the passivation of p-type crystalline silicon surfaces , 1998 .

[3]  B. Santo,et al.  Solid State , 2012 .

[4]  A. Stesmans.  Revision of H2 passivation of Pb interface defects in standard (111)Si/SiO2 , 1996 .

[5]  Stathis,et al.  Atomic hydrogen reactions with Pb centers at the (100) Si/SiO2 interface. , 1994, Physical review letters.

[6]  Weber,et al.  Dissociation energies of shallow-acceptor-hydrogen pairs in silicon. , 1989, Physical review. B, Condensed matter.

[7]  A. Stesmans.  Passivation of Pb0 and Pb1 interface defects in thermal (100) Si/SiO2 with molecular hydrogen , 1996 .

[8]  Andre Stesmans,et al.  Interaction of Pb defects at the (111)Si/SiO2 interface with molecular hydrogen: Simultaneous action of passivation and dissociation , 2000 .

[9]  Eduard A. Cartier,et al.  Anomalous positive charge formation by atomic hydrogen exposure , 1995 .

[10]  A. Stesmans,et al.  Hydrogen-induced thermal interface degradation in (111) Si/SiO2 revealed by electron-spin resonance , 1998 .

[11]  J. H. Stathis,et al.  Atomic hydrogen-induced degradation of the Si/SiO 2 structure , 1995 .

[12]  Eli Yablonovitch,et al.  A contactless minority lifetime probe of heterostructures, surfaces, interfaces and bulk wafers , 1992 .

[13]  B. O’Sullivan,et al.  Examination of the Si ( 111 ) ­ SiO2 , Si ( 110 ) ­ SiO2 , and Si ( 100 ) ­ SiO2 Interfacial Properties Following Rapid Thermal Annealing , 2002 .

[14]  Armin G. Aberle,et al.  Crystalline silicon solar cells : advanced surface passivation and analysis , 1999 .

[15]  K. Weber,et al.  Characterization of the Si − SiO2 Interface Following Room Temperature Ammonia Plasma Exposure , 2007 .

[16]  A. Goetzberger,et al.  Crystalline Silicon Solar Cells , 1998 .

[17]  Jacques I. Pankove,et al.  Neutralization of acceptors in silicon by atomic hydrogen , 1984 .

[18]  James H. Stathis,et al.  Passivation and depassivation of silicon dangling bonds at the Si/SiO2 interface by atomic hydrogen , 1993 .

[19]  A. Stesmans.  Comparative analysis of the H2 passivation of interface defects at the (100)SiSiO2 interface using electron spin resonance , 1996 .

[20]  R. Castagné,et al.  Description of the SiO2Si interface properties by means of very low frequency MOS capacitance measurements , 1971 .

[21]  Y. Onozawa,et al.  Effect of Hydrogen-Radical Annealing for SiO2 Passivation , 1996 .