The effect of activator concentration on the residual strength of alkali-activated fly ash pastes subjected to thermal load

Abstract This investigation reports on a comparative study of the residual compressive strength at different temperatures of alkali-activated fly ash (AAFA) pastes chemically activated using sodium silicate with three different concentrations named 20, 30 and 40 (wt.%). The behaviour of different mixtures in conditions of rapid temperature changes was studied. Water quench test was applied to determine thermal shock resistance. The traditional Portland cement pastes were used as a reference. The temperatures ranging from 200 °C to 1000 °C with an increment of 200 °C has been examined. Pore solution pH and compressive strengths before and after exposure to elevated temperatures were determined. The various decomposition phases formed were identified using X-ray diffraction (XRD), thermogravimetric analysis (TGA), differential thermal analysis (DTG) and scanning electron microscopy (SEM). The results indicated that fly ash activated by sodium silicate is more able to resist degradation caused by exposure to elevated temperature than Portland cement system as its relative strengths are superior. In the hardened AAFA pastes, as activator concentration dosage increased as the relative compressive strengths and thermal shock resistance decreased. The AAFA system is able to maintain a sufficient high pH to retain the passive protective layer on the surface of any reinforcing steel present.

[1]  M. Bussell Concrete and Reinforced Concrete , 2008 .

[2]  Caijun Shi,et al.  Stabilization/solidification of hazardous and radioactive wastes with alkali-activated cements. , 2006, Journal of hazardous materials.

[3]  Cengiz Duran Atiş,et al.  Influence of Activator on the Strength and Drying Shrinkage of Alkali-Activated Slag Mortar , 2009 .

[4]  Ángel Palomo,et al.  Alkali-activated fly ash: Effect of thermal curing conditions on mechanical and microstructural development – Part II , 2007 .

[5]  Ángel Palomo,et al.  Fixing Arsenic in Alkali‐Activated Cementitious Matrices , 2005 .

[6]  C. Alonso,et al.  Dehydration and rehydration processes of cement paste exposed to high temperature environments , 2004 .

[7]  B. Rangan,et al.  Sulfate and Acid Resistance of Fly Ash-based Geopolymer Concrete , 2005 .

[8]  Z. Bažant,et al.  Concrete at High Temperatures: Material Properties and Mathematical Models , 1996 .

[9]  Ángel Palomo,et al.  Mid-infrared spectroscopic studies of alkali-activated fly ash structure , 2005 .

[10]  Shao-dong Wang,et al.  Review of recent research on alkali-activated concrete in China , 1991 .

[11]  Á. Palomo,et al.  Durability of alkali-activated fly ash cementitious materials , 2007 .

[12]  Jay G. Sanjayan,et al.  Effect of elevated temperatures on geopolymer paste, mortar and concrete , 2010 .

[13]  M. Shoaib,et al.  Effect of fire and cooling mode on the properties of slag mortars , 2001 .

[14]  B. Vijaya Rangan,et al.  ON THE DEVELOPMENT OF FLY ASH-BASED GEOPOLYMER CONCRETE , 2004 .

[15]  B. Vijaya Rangan,et al.  Low-Calcium fly ash-based geopolymer concrete: Long-term properties , 2006 .

[16]  Kwesi Sagoe-Crentsil,et al.  Comparative performance of geopolymers made with metakaolin and fly ash after exposure to elevated temperatures , 2007 .

[17]  Keun-Hyeok Yang,et al.  Workability Loss and Compressive Strength Development of Cementless Mortars Activated by Combination of Sodium Silicate and Sodium Hydroxide , 2009 .

[18]  E. Douglas,et al.  A preliminary study on the alkali activation of ground granulated blast-furnace slag , 1990 .

[19]  F. C. Lea The resistance to fire of concrete and reinforced concrete , 1922 .

[20]  S. Macura,et al.  Structural characterization of pure Na-nephelines synthesized by zeolite conversion route , 2004 .

[21]  J.S.J. van Deventer,et al.  The potential use of geopolymeric materials to immobilise toxic metals: Part I. Theory and applications☆ , 1997 .

[22]  Sang-Sook Park,et al.  Characterization of fly ash-pastes synthesized at different activator conditions , 2008 .

[23]  Á. G. Torre,et al.  Quantitative determination of phases in the alkaline activation of fly ash. Part II: Degree of reaction , 2006 .

[24]  J. Deventer,et al.  Understanding the relationship between geopolymer composition, microstructure and mechanical properties , 2005 .

[25]  B. Talling Effect of Curing Conditions on Alkali-Activated Slags , 1989, "SP-114: Fly Ash, Silica Fume, Slag, and Natural Pozzolans in Concrete: Proceedings of the Third International Conference".

[26]  Pavel V. Krivenko,et al.  Directed synthesis of alkaline aluminosilicate minerals in a geocement matrix , 2007 .

[27]  M. Morsy,et al.  Effect of silica fume and metakaoline pozzolana on the performance of blended cement pastes against fire , 2007 .

[28]  J. Sanjayan,et al.  Behavior of combined fly ash/slag‐based geopolymers when exposed to high temperatures , 2009 .

[29]  Jay G. Sanjayan,et al.  Damage behavior of geopolymer composites exposed to elevated temperatures , 2008 .

[30]  D. Hasselman,et al.  Unified Theory of Thermal Shock Fracture Initiation and Crack Propagation in Brittle Ceramics , 1969 .

[31]  Y Zhang,et al.  DEVELOPMENT OF SUSTAINABLE CEMENTITIOUS MATERIALS , 2004 .

[32]  D. Hasselman,et al.  Elastic Energy at Fracture and Surface Energy as Design Criteria for Thermal Shock , 1963 .

[33]  V. M. Malhotra,et al.  HIGH PERFORMANCE HIGH VOLUME FLY ASH CONCRETE , 2002 .

[34]  G. A. Khoury,et al.  Material and environmental factors influencing the compressive strength of unsealed cement paste and concrete at high temperatures , 1993 .

[35]  R. Andersson,et al.  ALKALI-ACTIVATED SLAG , 1988 .

[36]  Karen L. Scrivener,et al.  Innovation in use and research on cementitious material , 2008 .

[37]  C. Real,et al.  Phase transformation on heating of an aged cement paste , 2004, 2401.14002.

[38]  Yong-Hee Choi,et al.  Physico-chemical properties of protein-bound polysaccharide from Agaricus blazei Murill prepared by ultrafiltration and spray drying process , 2007 .

[39]  Ángel Palomo,et al.  Alkali–aggregate reaction in activated fly ash systems , 2007 .

[40]  S. Chandrasekhar,et al.  Sintering behaviour of calcium exchanged low silica zeolites synthesized from kaolin , 2001 .

[41]  J. I. Escalante García,et al.  Cementitious composites of pulverised fuel ash and blast furnace slag activated by sodium silicate: effect of Na2O concentration and modulus , 2006 .

[42]  A M Rashad,et al.  EFFECT OF FIRE ON MICROSTRUCTURE AND MECHANICAL PROPERTIES OF BLENDED CEMENT PASTES CONTAINING METAKAOLIN AND SILICA FUME , 2008 .

[43]  S. Agarwal,et al.  Physicochemical, mineralogical, and morphological characteristics of concrete exposed to elevated temperatures , 2002 .

[44]  Ángel Palomo,et al.  Alkali-activated cementitious materials: Alternative matrices for the immobilisation of hazardous wastes: Part II. Stabilisation of chromium and lead , 2003 .

[45]  Ángel Palomo,et al.  Engineering Properties of Alkali-Activated Fly Ash Concrete , 2006 .

[46]  A. Fernández-Jiménez,et al.  A study on the passive state stability of steel embedded in activated fly ash mortars , 2008 .

[47]  J. Deventer,et al.  Geopolymer technology: the current state of the art , 2007 .

[48]  Ángel Palomo,et al.  Alkali-activated cementitous materials: Alternative matrices for the immobilisation of hazardous wastes Part I. Stabilisation of boron , 2003 .

[49]  T. Bakharev,et al.  Geopolymeric materials prepared using Class F fly ash and elevated temperature curing , 2005 .

[50]  A. Katz Microscopic study of alkali-activated fly ash , 1998 .