Modeling the failure of intermetallic/solder interfaces

Abstract Solder joint integrity is recognized as a key issue in the reliability of flip chip and ball grid arrays in integrated circuit packages. Significant reductions in the solder joint interconnect size results in both the increased volume fraction of brittle intermetallics in the joint and joule heating due to high current density. Previously, the prevalent failure mode in a solder joint was the ductile thermo-mechanical fracture of solder material due to repeated thermal cycling. In addition to this mode of failure the joints were also found to fail by brittle fracture near the solder–intermetallic interface. To predict and reduce the failure of solder joints, a model that incorporates both plastic damage in bulk solder and solder–intermetallic interface failure is timely and useful to the electronics industry. Based on cohesive fracture theory, a 3D finite element model has been developed to predict the interfacial damage of Sn–Ag–Cu eutectic lead-free solder interconnects. Unified creep-plasticity theory is incorporated in the model considering the creep and hysteresis effects in solder bulk. Using the unified creep-plasticity-cohesive finite element model, the intermetallic layer growth effect has been researched for different solders. The failure of solder is a complex, coupled thermo-electric-mechanical problem. To understand better the phenomenon, a thermo-electric finite element analysis has been conducted to predict the electrical concentration and joule heating effects on the failure of Sn–2.5Ag–0.8Cu–0.5Sb solder under different applied current densities. The temperature and current density distribution in a solder joint with a crack that propagates near the interface of the bulk solder and intermetallic layer has been predicted. Pronounced temperature and electrical current concentration are observed near the crack tip. Although the Pb-free solder is usually regarded as having a higher melting temperature compared with traditional Pb–Sn eutectic solder, the concentration of heat at the crack tip caused by joule heating may still melt the solder material under high current density stressing.

[1]  Y. C. Chan,et al.  High electric current density-induced interfacial reactions in micro ball grid array (μBGA) solder joints , 2006 .

[2]  K. Tu,et al.  Electromigration effect on intermetallic growth and Young’s modulus in SAC solder joint , 2006 .

[3]  Qingda Yang,et al.  A cohesive zone model for low cycle fatigue life prediction of solder joints , 2004 .

[4]  Systematic Design of Antireflection Coating for Semi-infinite One-dimensional Photonic Crystals Using Bloch Wave Expansion , 2002, cond-mat/0210405.

[5]  Michael Ortiz,et al.  A cohesive model of fatigue crack growth , 2001 .

[6]  Leon M Keer,et al.  Constitutive and damage model for a lead-free solder , 2001 .

[7]  Gautam Ghosh,et al.  Elastic properties, hardness, and indentation fracture toughness of intermetallics relevant to electronic packaging , 2004 .

[8]  S. Mhaisalkar,et al.  Investigation of cure kinetics and its effect on adhesion strength of nonconductive adhesives used in flip chip assembly , 2006, IEEE Transactions on Components and Packaging Technologies.

[9]  Shankar Mall,et al.  A cohesive zone model for fatigue crack growth in quasibrittle materials , 2001 .

[10]  D. McDowell,et al.  A Unified Creep-Plasticity Theory for Solder Alloys , 1994 .

[11]  King-Ning Tu,et al.  Relieving the current crowding effect in flip-chip solder joints during current stressing , 2006 .

[12]  T. R. Hsu,et al.  Mechatronics. An overview , 1997 .

[13]  John H. L. Pang,et al.  Electromigration induced ductile-to-brittle transition in lead-free solder joints , 2006 .

[14]  J. Shang,et al.  Effect of cooling rate on interfacial fatigue-crack growth in Sn-Pb solder joints , 1996 .

[15]  King-Ning Tu,et al.  Effect of current crowding on void propagation at the interface between intermetallic compound and solder in flip chip solder joints , 2006 .

[16]  T. Siegmund,et al.  An irreversible cohesive zone model for interface fatigue crack growth simulation , 2003 .

[17]  M. Benzeggagh,et al.  Measurement of mixed-mode delamination fracture toughness of unidirectional glass/epoxy composites with mixed-mode bending apparatus , 1996 .

[18]  Ganesh Subbarayan,et al.  A hybrid model for computationally efficient fatigue fracture simulations at microelectronic assembly interfaces , 2005 .

[19]  J. O. Suh,et al.  Effect of current crowding and Joule heating on electromigration-induced failure in flip chip composite solder joints tested at room temperature , 2005 .

[20]  Mgd Marc Geers,et al.  Fatigue damage modeling in solder interconnects using a cohesive zone approach , 2005 .

[21]  T. Mattila,et al.  Reliability of lead-free interconnections under consecutive thermal and mechanical loadings , 2006 .

[22]  Chih Chen,et al.  Infrared microscopy of hot spots induced by Joule heating in flip-chip SnAg solder joints under accelerated electromigration , 2006 .