Structural Evolution of Polyacrylonitrile Precursor Fibers during Preoxidation and Carbonization

SummaryStructural evolution of polyacrylonitrile precursor fibers during preoxidation and carbonization were studied using SEM combined with XRD, FTIR, elemental analysis and density measurement. Crystallite structure of fibers has been completely changed through the process. Crystallite size of fibers firstly increases before 235°, and then decreases with temperature increasing, whereas crystallinity gradually decreases during preoxidation. The combination between fibrils during preoxidation firstly becomes looser, and then gets denser. Meanwhile fibrils at first grow thicker, followed by getting thinner. Homogeneous and granular fracture surface of the resultant carbon fiber is obtained. Fracture morphology during the preparation undergoes transformation from ductile fracture feature to brittle fracture feature, which corresponds to changes of tensile strength and elongation at break from 0.865 GPa to 3.51 GPa, from 9.8% to 1.7%, respectively.

[1]  R. Moreton,et al.  Tensile Strengths of Carbon Fibres , 1974, Nature.

[2]  D. J. Johnson,et al.  Strength-structure relationships in PAN-based carbon fibres , 1983 .

[3]  A. Oberlin,et al.  Microtexture and structure of some high-modulus, PAN-base carbon fibres , 1984 .

[4]  S. Chand,et al.  Review Carbon fibers for composites , 2000 .

[5]  R. Young,et al.  Effect of fibre microstructure upon the modulus of PAN- and pitch-based carbon fibres , 1995 .

[6]  J. Donnet,et al.  Study of carbon fiber surfaces by scanning tunneling microscopy, part II—Pan-based high strength carbon fibers , 1993 .

[7]  G. Hinrichsen.  Structural changes of drawn polyacrylonitrile during annealing , 1972 .

[8]  A. Gupta,et al.  Effect of heat treatment on the structure and mechanical properties of polyacrylonitrile fibers , 1982 .

[9]  Chengguo Wang,et al.  HRTEM microstructures of PAN precursor fibers , 2006 .

[10]  L. M. Manocha,et al.  Characterization of oxidised pan fibres , 1974 .

[11]  D. J. Johnson.  Structure-property relationships in carbon fibres , 1987 .

[12]  W. Watt,et al.  Mechanism of oxidisation of polyacrylonitrile fibres , 1975, Nature.

[13]  Chengguo Wang,et al.  Influence of Precursor Properties on the Thermal Stabilization of Polyacrylonitrile Fibers , 2006 .

[14]  Ian R. Harrison,et al.  New aspects in the oxidative stabilization of PAN-based carbon fibers: II , 1996 .

[15]  Chengguo Wang,et al.  Combined Effect of Processing Parameters on Thermal Stabilization of PAN Fibers , 2006 .

[16]  A. Abhiraman,et al.  Conversion of acrylonitrile-based precursor fibres to carbon fibres , 1987 .

[17]  W. JOHNSON,et al.  Structure of High Modulus Carbon Fibres , 1967, Nature.