Characteristics of fracture during the approach process and wear mechanism of a silicon AFM tip.

The wear of an atomic force microscope (AFM) tip is one of the crucial issues in AFM as well as in other probe-based applications. In this work, wear tests under extremely low normal load using an AFM were conducted. Also, in order to understand the nature of silicon tip wear, the wear characteristics of crystal silicon and amorphous silicon oxide layer were investigated by a high-resolution transmission electron microscope (HRTEM). It was found that fracture of the tip readily occurred due to impact during the approach process. Experimental results showed that the impact should be below 0.1 nNs to avoid significant fracture of the tip. Also, it was observed that wear of the amorphous layer, formed at the end of the tip, occurred at the initial stage of the silicon tip damage process. Based on Archard's wear law, the wear coefficient of the amorphous layer was in the range of 0.009-0.014. As for the wear characteristics of the silicon tip, it was shown that wear occurred gradually under light normal load and the wear rate decreased with increase in the sliding distance. As for the wear mechanism of the silicon tip, oxidation wear was identified to be the most significant. It was shown that the degree of oxidation was higher under high normal load and in a nitrogen environment, oxidation of the silicon tip was reduced.

[1]  N. Amer,et al.  Simultaneous measurement of lateral and normal forces with an optical‐beam‐deflection atomic force microscope , 1990 .

[2]  Max G. Lagally,et al.  Comparison of wear characteristics of etched-silicon and carbon nanotube atomic-force microscopy probes , 2002 .

[3]  C. Quate,et al.  AUTOMATED PARALLEL HIGH-SPEED ATOMIC FORCE MICROSCOPY , 1998 .

[4]  Michael T. Postek,et al.  Modification of hydrogen-passivated silicon by a scanning tunneling microscope operating in air , 1990 .

[5]  Håkan Olin,et al.  Force interactions and adhesion of gold contacts using a combined atomic force microscope and transmission electron microscope , 2002 .

[6]  Dong F. Wang,et al.  Nano-Scale Fatigue Wear of Carbon Nitride Coatings: Part II—Wear Mechanisms , 2003 .

[7]  Rutland,et al.  Tip friction - torsional spring constant determination. , 2000, Colloids and surfaces. B, Biointerfaces.

[8]  D. Rugar,et al.  Thermomechanical writing with an atomic force microscope tip , 1992 .

[9]  J. Zou,et al.  Microstructures of phases in indented silicon: A high resolution characterization , 2003 .

[10]  U. Hartmann,et al.  Scratching resistance of diamond-like carbon coatings in the subnanometer regime , 1999 .

[11]  S. Hosaka,et al.  SPM-based data storage for ultrahigh density recording , 1997 .

[12]  R. Prioli,et al.  Correlation between nano-scale friction and wear of boron carbide films deposited by dc-magnetron sputtering , 1999 .

[13]  K. Katô,et al.  Wear of the atomic force microscope tip under light load, studied by atomic force microscopy , 1995 .

[14]  Dae-Eun Kim,et al.  Fundamental Investigation of Micro Wear Rate Using an Atomic Force Microscope , 2003 .

[15]  B. Bhushan,et al.  Micro/nanotribological studies of polysilicon and SiC films for MEMS applications , 1998 .

[16]  Hal Edwards,et al.  Vertical metrology using scanning-probe microscopes: Imaging distortions and measurement repeatability , 1998 .

[17]  Miss A.O. Penney.  (b) , 1974, The New Yale Book of Quotations.

[18]  Spain,et al.  Crystal data for high-pressure phases of silicon. , 1986, Physical review. B, Condensed matter.

[19]  John Alexander,et al.  Nanometer-scale lithography using the atomic force microscope , 1992 .

[20]  B. Terris,et al.  Atomic force microscope-based data storage: track servo and wear study , 1998 .

[21]  T. Kizuka.  Atomic Process of Point Contact in Gold Studied by Time-Resolved High-Resolution Transmission Electron Microscopy , 1998 .

[22]  Koji Kato,et al.  Wear of the AFM diamond tip sliding against silicon , 1997 .

[23]  G. Abadal,et al.  AFM lithography of aluminum for fabrication of nanomechanical systems. , 2003, Ultramicroscopy.

[24]  R. Howe,et al.  Critical Review: Adhesion in surface micromechanical structures , 1997 .

[25]  Robert Hull,et al.  Properties of Crystalline Silicon , 1999 .

[26]  Growth of a single-wall carbon nanotube in the gap of scanning tunneling microscope , 1999 .

[27]  Jun Hu,et al.  ATOMIC-SCALE FRICTION AND WEAR OF MICA , 1995 .

[28]  Andrew G. Glen,et al.  APPL , 2001 .

[29]  Ernst Meyer,et al.  Friction on the atomic scale: An ultrahigh vacuum atomic force microscopy study on ionic crystals , 1996 .

[30]  Jean-Pierre Celis,et al.  Calibration procedures for frictional measurements with a lateral force microscope , 1996 .

[31]  C. Quate,et al.  Parallel atomic force microscopy using cantilevers with integrated piezoresistive sensors and integrated piezoelectric actuators , 1995 .