Crack influence on load-bearing capacity of glued laminated timber using extended finite element modelling

Abstract Most of the cracks are caused by changes in temperature and relative humidity which lead to shrinkage and swelling of the wood and thereby induce stresses in the structure. How these cracks influence the strength of the wooden structure, especially the shear strength, is not well understood. However, it is reasonable to expect that cracks have an impact on the shear strength as they preferably run along the beams in the direction of grain and bond lines. The purpose of this study was to investigate the load-bearing capacity of cracked glulam beams and to find a model that could predict the failure load of the beams due to the cracks. Three-point bending tests were used on glulam beams of different sizes with pre-manufactured cracks. An orthotropic elastic model and extended finite element method was used to model the behaviour of the cracked beams and to estimate the load-bearing capacity. The conclusions were validated by numerical simulations of the mechanical behaviour of three-point bending of glulam beams with different crack locations. The crack initiation load was recorded as the failure load and compared to the experimental failure load. The results of the compaction simulations agree well with the experimental results.

[1]  José Morais,et al.  Mode II wood fracture characterization using the ELS test , 2007 .

[2]  Michael Kaliske,et al.  Models for numerical failure analysis of wooden structures , 2009 .

[3]  John W. Hutchinson,et al.  Fracture and Fatigue , 1982 .

[4]  José Morais,et al.  Comparison of fracture properties of two wood species through cohesive crack simulations , 2008 .

[5]  Zhongwei Guan,et al.  Nonlinear Finite Element Modeling of Crack Behavior in Oriented Strand Board Webbed Wood I-Beams with Openings , 2004 .

[6]  E. Zhu,et al.  Fracture Toughness of Northeast China Larch , 2012 .

[7]  L. Daudeville,et al.  Fracture in spruce: experiment and numerical analysis by linear and non linear fracture mechanics , 1999, Holz als Roh- und Werkstoff.

[8]  Ted Belytschko,et al.  A method for dynamic crack and shear band propagation with phantom nodes , 2006 .

[9]  Meng Gong,et al.  Fracture and fatigue in wood , 2003 .

[10]  I. Babuska,et al.  The partition of unity finite element method: Basic theory and applications , 1996 .

[11]  L. Mishnaevsky,et al.  Damage evolution in nanoclay-reinforced polymers: A three-dimensional computational study , 2013 .

[12]  M.F.S.F. de Moura,et al.  Numerical analysis of the ENF test for mode II wood fracture , 2006 .

[13]  P. Quenneville,et al.  Analysis of the fracture behavior of Radiata Pine timber and Laminated Veneer Lumber , 2014 .

[14]  H. Yoshihara,et al.  Mode I and Mode II fracture toughness of densified Sitka spruce fabricated in an airtight atmosphere with high-temperature steam , 2007 .

[15]  L. Daudeville,et al.  Prediction of the load carrying capacity of bolted timber joints , 1999, Wood Science and Technology.

[16]  Pem Electrodes,et al.  ON DAMAGE EVOLUTION OF , 2010 .

[17]  S. Fortino,et al.  A simple approach for FEM simulation of Mode I cohesive crack growth in glued laminated timber under short-term loading , 2012 .

[18]  Ted Belytschko,et al.  Elastic crack growth in finite elements with minimal remeshing , 1999 .

[19]  S. Stanzl-Tschegg,et al.  New splitting method for wood fracture characterization , 2004, Wood Science and Technology.

[20]  Robert J. Ross,et al.  Wood handbook : wood as an engineering material , 2010 .

[21]  S. Stanzl-Tschegg,et al.  Mode III fracture energy of wood composites in comparison to solid wood , 1999, Wood Science and Technology.

[22]  L. Broutman,et al.  Fracture and fatigue , 1974 .

[23]  A. Needleman,et al.  The simulation of dynamic crack propagation using the cohesive segments method , 2008 .

[24]  M. Ekevad,et al.  Shear Resistance of Glulam Beams with Cracks , 2012 .