Spalling behavior of metakaolin-fly ash based geopolymer concrete under elevated temperature exposure

Abstract Fire-induced spalling is a serious risk to concrete structures, especially for high strength concrete structures. This paper presents results from high temperature spalling tests on geopolymer concrete. The effect of moisture content, concrete strength, heating rate and temperature level on the spalling behavior of geopolymer concrete is studied. The temperature-induced spalling mechanism in geopolymer concrete is investigated through the measurement of residual compressive and splitting tensile strength, variation in permeability (by sorptivity test) and chemical composition (by X-ray diffraction test) of geopolymer concrete after elevated temperature exposure up to 700 °C. The test results indicate that geopolymer concrete exhibit a good spalling resistance as compared to that of OPC concrete. The lower spalling risk in geopolymer concrete under high temperature exposure is facilitated from the highly connected pore structures and lower strength degradation with temperatures. Further results indicate that the pore structure (permeability) of geopolymer concrete gets a significant evolution with the exposure temperature, especially above 500 °C range. This is related to the sintering reaction in geopolymer binders at high temperatures.

[1]  Sun-Jong Park,et al.  Evaluation of residual tensile strength of fire-damaged concrete using a non-linear resonance vibration method , 2015 .

[2]  Z. Tao,et al.  In Situ Elevated Temperature Testing of Fly Ash Based Geopolymer Composites , 2016, Materials.

[3]  W. Rickard,et al.  Performance of solid and cellular structured fly ash geopolymers exposed to a simulated fire , 2014 .

[4]  F. Delhomme,et al.  An experimental method for assessing the spalling sensitivity of concrete mixture submitted to high temperature , 2012 .

[5]  J. Deventer,et al.  The Role of Inorganic Polymer Technology in the Development of ‘Green Concrete’ , 2007 .

[6]  J. Deventer,et al.  Thermal evolution of metakaolin geopolymers: Part 1 – Physical evolution , 2006 .

[7]  N. Carino,et al.  Effects of Test Conditions and Mixture Proportions on Behavior of High-Strength Concrete Exposed to High Temperatures , 2002 .

[8]  Kang Hai Tan,et al.  A new perspective on nature of fire-induced spalling in concrete , 2018, Construction and Building Materials.

[9]  V. Kodur,et al.  Comparative Thermal and Mechanical Performance of Geopolymers derived from Metakaolin and Fly Ash , 2016 .

[10]  M. Fontana,et al.  Concrete Permeability and Explosive Spalling in Fire , 2016 .

[11]  Ruby Mejía de Gutiérrez,et al.  Performance of geopolymer concrete composed of fly ash after exposure to elevated temperatures , 2017 .

[12]  Faiz Shaikh,et al.  Compressive strength of fly‐ash‐based geopolymer concrete at elevated temperatures , 2015 .

[13]  Toshiro Kamada,et al.  Study of mechanisms of explosive spalling in high-strength concrete at high temperatures using acoustic emission , 2012 .

[14]  Venkatesh Kodur,et al.  Thermal behavior and mechanical properties of geopolymer mortar after exposure to elevated temperatures , 2016 .

[15]  Y. N. Chan,et al.  Residual strength and pore structure of high-strength concrete and normal strength concrete after exposure to high temperatures , 1999 .

[16]  Jay G. Sanjayan,et al.  Geopolymer and Portland cement concretes in simulated fire , 2011 .

[17]  Albert Noumowe,et al.  Spalling, Thermal, and Hydrous Behavior of Ordinary and High-Strength Concrete Subjected to Elevated Temperature , 2011 .

[18]  Grant C. Lukey,et al.  Physical evolution of Na-geopolymer derived from metakaolin up to 1000 °C , 2007 .

[19]  Pierre Kalifa,et al.  High-temperature behaviour of HPC with polypropylene fibres: From spalling to microstructure , 2001 .

[20]  J. Sanjayan,et al.  Effect of aggregate size on spalling of geopolymer and Portland cement concretes subjected to elevated temperatures , 2012 .

[21]  Ronan Hébert,et al.  Influence of the nature of aggregates on the behaviour of concrete subjected to elevated temperature , 2011 .

[22]  Lianchong Li,et al.  Study on mechanism of thermal spalling in concrete exposed to elevated temperatures , 2011 .

[23]  W. Rickard,et al.  Thermally Induced Microstructural Changes in Fly Ash Geopolymers: Experimental Results and Proposed Model , 2015 .

[24]  Venkatesh Kodur,et al.  Properties of Concrete at Elevated Temperatures , 2014 .

[25]  J. Davidovits.  Geopolymers : inorganic polymeric new materials , 1991 .

[26]  Stephan Pirskawetz,et al.  Acoustic emission and microstructural changes in fly ash geopolymer concretes exposed to simulated fire , 2016 .

[27]  V. Kodur,et al.  Development of metakaolin–fly ash based geopolymers for fire resistance applications , 2014 .

[28]  Hui Zhou,et al.  Experimental investigations on loading-rate dependency of compressive and tensile mechanical behaviour of hard rocks , 2015 .

[29]  Gary R. Consolazio,et al.  Measurement and Prediction of Pore Pressures in Saturated Cement Mortar Subjected to Radiant Heating , 1998 .

[30]  O. Kayali,et al.  Performance of fly ash based geopolymer concrete made using non-pelletized fly ash aggregates after exposure to high temperatures , 2015 .

[31]  Venkatesh Kodur,et al.  Critical factors governing the fire performance of high strength concrete systems , 2007 .

[32]  Shaoxian Song,et al.  Geopolymerization reaction, microstructure and simulation of metakaolin-based geopolymers at extended Si/Al ratios , 2017 .

[33]  Faiz Shaikh.  Mechanical properties of concrete containing recycled coarse aggregate at and after exposure to elevated temperatures , 2018 .

[34]  P. Sarker,et al.  Effect of fire exposure on cracking, spalling and residual strength of fly ash geopolymer concrete , 2014 .