Concentration profiles through a duplex oxide grown on 316 stainless steel

Concentration profiles through duplex scales formed on vacuum annealed 316 stainless steel have been investigated using neutron activation analysis and energy dispersive analysis. Good qualitative agreement between the two analytical techniques was obtained for chromium concentration profiles in the outer oxide. These indicated a low rate of chromium diffusion into the Fe3O4 layer. There was less agreement between the two methods in the inner oxide as the neutron activation results were complicated by the presence of metal in sections through this oxide layer. The energy dispersive results in this layer were consistent with previous findings which indicated conservative or non selective oxidation occurring. Konzentrationsprofile in einem Duplex-Oxidzunder auf Stahl 316 Konzentrationsprofile in auf vakuumangelassenem Stahl 316 entstandenem Duplex-Oxidzunder wurden mit Neutronenaktivierungsanalyse und energiedispersiver Analyse untersucht. Gute qualitative Ubereinstimmung zwischen den beiden Methoden ergab sich fur das Konzentrationsprofil von Chrom in der auseren Oxidschicht; die Ergebnisse deuten auf eine geringe Geschwindigkeit der Stromdiffusion in die ausere Magnetitschicht. Bei der inneren Oxidschicht ist die Ubereinstimmung zwischen den beiden Methoden weniger gut, da die Ergebnisse der Neutronenaktivierung durch die Anwesenheit von Metall in der Querschnittsflache verfalscht werden. Die Ergebnisse der energiedispersiven Analysen dieser Schicht stimmen mit fruheren Befunden uberein, wonach normale oder nichtselektive Oxydation auftritt.