Synthesis Optimization and Performance Test of Environmentally Friendly Renewable Poly(HMA-co-BMA-co-MA) Oil Absorbing Microspheres

In this study, butyl methacrylate (BMA), methyl acrylate (MA), cetyl methacrylate (HMA) as monomers, cetyl trimethyl ammonium bromide (CTAB) as dispersant, benzoyl peroxide (BPO) as initiator,N, n-methylene diacrylamide (MBA) as crosslinking agent, A kind of ternary oil absorbing resin was prepared by suspension polymerization. The range of long chain monomer (HMA), initiator (BPO), crosslinking agent (MBA) and surfactant (CTAB) was optimized by single factor experiment, and the best resin Poly (HMA-co-BMA-Co-MA) was obtained by orthogonal experiment design. The structure was analyzed by FR-IR, the microstructure of the resin was observed by SEM, and the stability of the resin was evaluated by TG. The experiment showed that the influence degree of reaction factors was as follows: long chain monomer amount > initiator amount > crosslinking agent amount > dispersant amount. The optimal synthesis conditions were: long chain monomer =25wt%, initiator =1wt%, crosslinking agent =1.1wt%, dispersant =0.030g.

[1]  N. Al‐Ansari,et al.  Acute toxicity of the water chlorination byproduct (chloroform) in male mice , 2020 .

[2]  Yuanzhu Mi,et al.  Demulsification of Water-Containing Crude Oil Driven by Environmentally Friendly SiO2@CS Composite Materials , 2020 .

[3]  Luyao Ren,et al.  Eco-friendly separation layers based on waste peanut shell for gravity-driven water-in-oil emulsion separation , 2020 .

[4]  C. Zhang,et al.  Synthesis of MnO2/poly(n-butylacrylate-co-butyl methacrylate-co-methyl methacrylate) hybrid resins for efficient oils and organic solvents absorption , 2017 .

[5]  Li Yan,et al.  Synthesis and Absorption Performance of Acrylic Ester and Hollow Fiber MgO Nanoparticle Resin Composite , 2017 .

[6]  Tao Zhang,et al.  Synthesis and oil absorption of biomorphic MgAl Layered Double Oxide/acrylic ester resin by suspension polymerization , 2016 .

[7]  Chuan-jiang Liu,et al.  Precontrol of algae-induced black blooms through sediment dredging at appropriate depth in a typical eutrophic shallow lake , 2015 .

[8]  Q. Xue,et al.  A versatile approach to produce superhydrophobic materials used for oil-water separation. , 2014, Journal of colloid and interface science.

[9]  Hou Chen,et al.  Preparation of High Oil Absorption Resins by Suspended Emulsion Polymerization and Their Properties , 2013 .

[10]  Yi Lu,et al.  Fabrication of porous carbon nitride foams/acrylic resin composites for efficient oil and organic solvents capture , 2019, Chemical Engineering Journal.