Rheometry of aging of colloidal melamine-urea-formaldehyde polycondensates

Aged and whitened melamine–urea–formaldehyde (MUF) resins in a colloidal state were tested with parallel-plate rheometry to determine the extent of their viscoelastic behavior. Only in advanced colloidal states, and so only when aggregated colloidal clusters occurred, did the resins present clear indications of viscoelastic responses, as illustrated by the crossover of elastic modulus and viscous modulus curves at lower strain percentages. These colloidal clusters were labile microstructures, which, broken by applied shear, justified the known thixotropic behavior of these resins sufficiently advanced by aging or other means. MUF resins already in the colloidal state, but for which colloidal clustering had not yet occurred, behaved exclusively as viscous liquids. Two different cases of physical gelation were observed, reversible physical gelation and irreversible physical gelation, underlying which a true gel situation possibly occurred. Physical gelation due to colloidal superstructures occurred in both, but the difference in the resin average molecular masses revealed if the physical gelation was reversible or irreversible and, therefore, if the liquid/cluster separation was defined as the terminal phase of physical gelation. © 2005 Wiley Periodicals, Inc. J Appl Polym Sci 96: 655–659, 2005

[1]  A. Pizzi,et al.  Dependance on the adhesive formulation of the upgrading of MUF particleboard adhesives and decrease of melamine content by buffer and additives , 2004, Holz als Roh- und Werkstoff.

[2]  A. Pizzi,et al.  Low-volatility acetals to upgrade the performance of melamine-urea-formaldehyde wood adhesive resins , 2004 .

[3]  A. Pizzi,et al.  Colloidal aggregation of MUF polycondensation resins: Formulation influence and storage stability , 2004 .

[4]  A. Pizzi,et al.  Acetals-induced strength increases and lower resin content in MUF and PE wood adhesives , 2003, Holz als Roh- und Werkstoff.

[5]  A. Pizzi,et al.  Upgrading of MUF polycondensation resins by buffering additives. II. Hexamine sulfate mechanisms and alternate buffers , 2003 .

[6]  A. Pizzi,et al.  Upgrading melamine–urea–formaldehyde polycondensation resins with buffering additives. I. The effect of hexamine sulfate and its limits , 2003 .

[7]  A. Pizzi,et al.  Structure effects of additives in performance improvement of aminoplastic adhesive resins , 2003 .

[8]  M. Zanetti,et al.  Qualitätssteigerung von MUF-Harzen für Spanplatten und Verringerung des Melaningehaltes durch Puffer und Zusätze , 2003 .

[9]  A. Pizzi,et al.  Upgrading of MUF particleboard adhesives and decrease of melamine content by buffer and additives , 2003, Holz als Roh- und Werkstoff.

[10]  A. Pizzi,et al.  Acetals‐induced strength increase of melamine–urea–formaldehyde (MUF) polycondensation adhesives. II. Solubility and colloidal state disruption , 2002 .

[11]  Antonio Pizzi,et al.  Acetal‐induced strength increases and lower resin content of MUF and other polycondensation adhesives , 2002 .

[12]  V. Litvinov,et al.  Physical gelation of melamine formaldehyde resin solutions. II. A combined light‐scattering and low‐resolution relaxation proton NMR study , 1999 .

[13]  A. Pizzi,et al.  A 13C NMR study of polyflavonoid tannin adhesive intermediates. II. Colloidal state reactions , 1994 .

[14]  A. Dunker,et al.  Slightly Bizarre Protein Chemistry: Urea-Formaldehyde Resin from a Biochemical Perspective , 1986 .

[15]  W. Johns,et al.  A Novel Concept on the Structure of Cured Urea-Formaldehyde Resin , 1985 .