Effects of pretreatment processes on improving the formation of ultrananocrystalline diamond

Effects of pretreatment on the nuclei formation of ultrananocrystalline diamond (UNCD) on Si substrates were studied. Either precoating a thin layer of titanium (∼400nm) or ultrasonication pretreatment using diamond and titanium mixed powder (D&T process) enhances the nucleation process on Si substrates markedly, and the UNCD nuclei formed and fully covered the Si substrate, when deposition was processed using the microwave-plasma-enhanced chemical-vapor deposition process for 10min. In contrast, during the same period, ultrasonication pretreatment using diamond powders (D process) can only form large UNCD clusters, which were scarcely distributed on Si substrates. The analyses using x-ray diffractometer, secondary ion mass spectroscopy, and electron spectroscopy for chemical analysis reveal that the titanium layer reacted with carbon species in the plasma, forming crystalline TiC phase, which facilitates the subsequent formation of UNCD nuclei. The beneficial effect of Ti layer on enhancing the nucleatio...

[1]  D. Gruen,et al.  Bonding structure in nitrogen doped ultrananocrystalline diamond , 2003 .

[2]  D. Gruen,et al.  Morphology and electronic structure in nitrogen-doped ultrananocrystalline diamond , 2002 .

[3]  Omar Elmazria,et al.  Surface acoustic wave propagation in aluminum nitride-unpolished freestanding diamond structures , 2002 .

[4]  J. Robertson,et al.  Origin of the 1 1 5 0 − cm − 1 Raman mode in nanocrystalline diamond , 2001 .

[5]  Zhili Sun,et al.  UV Raman characteristics of nanocrystalline diamond films with different grain size , 2000 .

[6]  Dieter M. Gruen,et al.  NANOCRYSTALLINE DIAMOND FILMS1 , 1999 .

[7]  Jin,et al.  Low-field electron emission from undoped nanostructured diamond , 1998, Science.

[8]  T. Y. Wang,et al.  Novel two stage method for growth of highly transparent nano-crystalline diamond films , 1998 .

[9]  A. Hoffman,et al.  Kinetics of the initial stages of CVD diamond growth on non-diamond substrates: surface catalytic effects and homoepitaxy , 1997 .

[10]  A. Hoffman,et al.  Mechanism of diamond formation on substrates abraded with a mixture of diamond and metal powders , 1996 .

[11]  D. Dandy,et al.  Studies on nucleation process in diamond CVD: an overview of recent developments , 1995 .

[12]  A. Hoffman,et al.  Enhancement of diamond nucleation by ultrasonic substrate abrasion with a mixture of metal and diamond particles , 1995 .

[13]  J. Glass,et al.  Textured growth of diamond on silicon via in situ carburization and bias‐enhanced nucleation , 1993 .

[14]  M. Couzi,et al.  Influence on diamond nucleation of the carbon concentration near the substrate surface , 1993 .

[15]  R. Messier,et al.  Current Issues and Problems in the Chemical Vapor Deposition of Diamond , 1990, Science.

[16]  Hans Kuzmany,et al.  The mystery of the 1140 cm−1 Raman line in nanocrystalline diamond films , 2004 .

[17]  A. Hoffman,et al.  Influence of Ti, Fe, and Cu metal submicron-particles on diamond CVD on Si substrates , 2000 .