Stress corrosion cracking and hydrogen embrittlement of an Al–Zn–Mg–Cu alloy

The age hardening, stress corrosion cracking (SCC) and hydrogen embrittlement (HE) of an Al-Zn-Mg-Cu 7175 alloy were investigated experimentally. There were two peak-aged states during ageing. For ageing at 413 K, the strength of the second peak-aged state was slightly higher than that of the first one, whereas the SCC susceptibility was lower, indicating that it is possible to heat treat 7175 to high strength and simultaneously to have high SCC resistance. The SCC susceptibility increased with increasing Mg segregation at the grain boundaries. Hydrogen embrittlement (HE) increased with increased hydrogen charging and decreased with increasing ageing time for the same hydrogen charging conditions. Computer simulations were carried out of (a) the Mg grain boundary segregation using the embedded atom method and (b) the effect of Mg and H segregation on the grain boundary strength using a quasi-chemical approach. The simulations showed that (a) Mg grain boundary segregation in Al-Zn-Mg-Cu alloys is spontaneous, (b) Mg segregation decreases the grain boundary strength, and (c) H embrittles the grain boundary more seriously than does Mg. Therefore, the SCC mechanism of Al-Zn-Mg-Cu alloys is attributed to the combination of HE and Mg segregation induced grain boundary embrittlement.

[1]  T. Magnin,et al.  Influence of critical surface defects and localized competition between anodic dissolution and hydrogen effects during stress corrosion cracking of a 7050 aluminium alloy , 1997 .

[2]  N. Holroyd,et al.  Strain-rate effects in the environmentally assisted fracture of a commercial high-strength aluminium alloy (7049) , 1981 .

[3]  Foiles,et al.  Embedded-atom-method functions for the fcc metals Cu, Ag, Au, Ni, Pd, Pt, and their alloys. , 1986, Physical review. B, Condensed matter.

[4]  P. Adler,et al.  Influence of microstructure on the mechanical , 1972 .

[5]  V. Vítek,et al.  A computer simulation study of (001) and (111) tilt boundaries: The multiplicity of structures , 1984 .

[6]  Joshua R. Smith,et al.  Universal features of the equation of state of metals , 1984 .

[7]  B. Shollock,et al.  On the structure and composition of G-P zones in high purity AlZnMg alloys , 1988 .

[8]  R. K. Viswanadham,et al.  Grain boundary segregation in Al-Zn-Mg alloys—Implications to stress corrosion cracking , 1980 .

[9]  D. Laughlin,et al.  The Effect of Solute Content on the Slip Behavior in 7XXX Series Aluminum Alloys , 1981 .

[10]  R. LeSar,et al.  SEGREGATION TO AND STRUCTURE OF (001) TWIST GRAIN BOUNDARIES IN Cu-Ni ALLOYS , 1993 .

[11]  P. S. Pao,et al.  The role of magnesium in CF and SCC of 7000 series aluminum alloys , 1984 .

[12]  Russel H. Jones,et al.  Role of Mg in the stress corrosion cracking of an Al-Mg alloy , 2001 .

[13]  S. Ranganathan,et al.  On the geometry of coincidence‐site lattices , 1966 .

[14]  A. Voter,et al.  Investigation of the effects of boron on Ni_3Al grain boundaries by atomistic simulations , 1990 .

[15]  S. Pyun,et al.  A critical evaluation of the stress-corrosion cracking mechanism in high-strength aluminum alloys , 1991 .

[16]  B. Chalmers,et al.  A coincidence — Ledge — Dislocation description of grain boundaries , 1968 .

[17]  I. Bernstein,et al.  The role of microstructure in hydrogen-assisted fracture of 7075 aluminum , 1979 .

[18]  G. Koch.  Hydrogen Induced Fracture of a High Strength Aluminum Alloy , 1979 .

[19]  J. Liu,et al.  Grain boundary segregation and hydrogen-induced fracture in 7050 aluminium alloy , 1996 .

[20]  G. Scamans.  Evidence for crack-arrest markings on intergranular stress corrosion fracture surfaces in Al-Zn-Mg alloys , 1980 .

[21]  T. Turmezey,et al.  Direct observation of ordered Guinier-Preston zones in an AlZnMg alloy , 1981 .

[22]  J. Lumsden,et al.  The Stress Corrosion Cracking Behavior of AlLi Alloy 8090 , 1988 .

[23]  N. Christensen.  Relativistic band structure calculations , 1984 .

[24]  J. Hatch,et al.  Aluminum: Properties and Physical Metallurgy , 1984 .

[25]  M. Doyama,et al.  The relation between the formation energy of a vacancy and the nearest neighbor interactions in pure metals and liquid metals , 1976 .

[26]  M. Baskes,et al.  Embedded-atom method: Derivation and application to impurities, surfaces, and other defects in metals , 1984 .

[27]  C. Buckley,et al.  Hydrogen in aluminum , 1997 .

[28]  Li-Ping Zheng,et al.  Monte Carlo simulation of Mg segregation to Ni3Al grain boundary , 2000 .

[29]  G. Scamans.  Discontinuous propagation of stress corrosion cracks in AlZnMg alloys , 1979 .

[30]  A. Ardell,et al.  Microstructures of the commercial 7075 Al alloy in the T651 and T7 tempers , 1983 .

[31]  T. Magnin,et al.  Hydrogen effects during IGSCC of pure Al–5Mg alloy in NaCl media , 2002 .

[32]  J. Gjønnes,et al.  An electron microscope investigation of the microstructure in an aluminium-zinc-magnesium alloy , 1970 .

[33]  A. Voter,et al.  Computer simulation on surfaces and [001] symmetric tilt grain boundaries in Ni, Al, and Ni_3Al , 1989 .

[34]  T. Magnin.  Recent Advances in the Environment Sensitive Fracture Mechanisms of Aluminium Alloys , 1996 .

[35]  J. M. Chen,et al.  Grain boundary segregation of an Al-Zn-Mg ternary alloy , 1977 .

[36]  H. Jiao,et al.  The HREM study of precipitates in an Al−Zn−Mg alloy , 1995 .

[37]  M. Elices,et al.  Microstructure and susceptibility to stress corrosion cracking of AlZnMg weldments (AA-7017) , 1994 .

[38]  P. Swann,et al.  Pre-exposure embrittlement and stress corrosion failure in AlZnMg Alloys , 1976 .

[39]  H. Flower,et al.  Hydrogen embrittlement and trapping in Al6%Zn-3%Mg , 1980 .

[40]  Arthur F. Voter,et al.  Accurate Interatomic Potentials for Ni, Al and Ni3Al , 1986 .

[41]  A. Zieliński,et al.  Effect of microstructure on stress corrosion cracking of an Al-Zn-Mg-Cu alloy , 1998 .

[42]  B. Ralph,et al.  A field ion microscope study of atomic configuration at grain boundaries , 1964 .

[43]  J. Robinson.  Influence of Retrogressing and Reaging on the Stress Corrosion Cracking Resistance of 7010 , 2000 .

[44]  V. Vítek,et al.  Relationships between grain boundary structure and energy , 1986 .

[45]  J. Scully,et al.  The effects of test temperature, temper, and alloyed copper on the hydrogen-controlled crack growth rate of an Al-Zn-Mg-(Cu) alloy , 2000 .

[46]  J. B. Sande,et al.  A transmission electron microscopy investigation of the early stages of precipitation in an Al-Zn-Mg alloy , 1976 .

[47]  W. Precht,et al.  Preparation and properties of VC + Ni cermets with controlled carbon-to-metal ratio , 1980 .

[48]  B. Legrand,et al.  How to compare superficial and intergranular segregation? A new analysis within the mixed SMA–TBIM approach , 1999 .

[49]  M. Seah.  Adsorption-induced interface decohesion , 1980 .

[50]  E. Lavernia,et al.  Tension and compression of bulk Al-7.5 wt% Mg alloy , 2003 .

[51]  S. Lynch.  Environmentally Assisted Cracking: Overview of Evidence for an Adsorption-Induced Localised-Slip Process, , 1988 .

[52]  G. M. Bond,et al.  The influence of hydrogen on deformation and fracture processes in high-strength aluminum alloys , 1987 .