The Effect of SiC Coating on the Joint of C/C and LAS

The SiC coating on C/C composites was prepared by CVD and pack-cementation method in this paper, then SiC coated C/C composites was jointed with LAS glass ceramic at 1423K for 30min and the pressure of 15 MPa. The structure and morphology of the SiC coating and as-received joints were analyzed by SEM and XRD; shear strength of joint was examined through the Instron universal testing tensile machine. The results show that the thickness of SiC coating prepared by CVD is about 30μm, while the thickness of SiC layer by pack-cementation is nearly 100μm, and the layer is easier to connect with LAS glass ceramic owing to the rough surface and wedge-shaped structure on the SiC coating; the shear strength of joint between SiC coating coated C/C and LAS by pack-cementation is greater than the joint of C/C- LAS with SiC coating prepared by CVD.

[1]  B. Revel,et al.  MAS-NMR studies of lithium aluminum silicate (LAS) glasses and glass–ceramics having different Li2O/Al2O3 ratio , 2010 .

[2]  Zhou Wancheng,et al.  Microstructure and Dielectric Properties of Chopping SiCf/LAS Composites , 2009 .

[3]  C. Composites.  Joining of Surface Modified Carbon/Carbon Composites and LAS Glass Ceramic , 2009 .

[4]  Jinglong Li,et al.  Transient liquid-phase diffusion bonding of two-dimensional carbon–carbon composites to niobium alloy , 2008 .

[5]  Hejun Li,et al.  Vitreous joining of SiC-coated carbon/carbon composites , 2008 .

[6]  Ling-jun Guo,et al.  Novel thermal gradient chemical vapor infiltration process for carbon-carbon composites , 2007 .

[7]  Li Kezhi,et al.  A new SiC/yttrium silicate/glass multi-layer oxidation protective coating for carbon/carbon composites , 2004 .

[8]  M. Ferraris,et al.  Joining of Carbon‐Carbon Composites for Thermonuclear Fusion Applications. , 1997 .

[9]  M. Ferraris,et al.  Joining of Carbon‐Carbon Composites for Thermonuclear Fusion Applications , 1997 .

[10]  P. Dadras,et al.  Joining of Carbon—Carbon Composites Using Boron and Titanium Disilicide Interlayers , 1997 .

[11]  J. Baptista,et al.  Low-temperature sintering of silicon carbide with Li2O-Al2O3-SiO2 melts as sintering aids , 1996 .

[12]  Peter F. James,et al.  Glass ceramics: new compositions and uses , 1995 .

[13]  S. A. Dunn,et al.  The effect of boria and titania addition on the crystallization and sintering behavior of Li2O-Al2O3-4SiO2 glass , 1994 .