Mechanochemical effects on the properties of starting mixtures for PbTiO3 ceramics by using a novel grinding equipment

The effects of milling were studied using a newly developed multi-ring media-type grinding machine on the synthesis processes of PbTiO3 ceramics from PbO-TiO2 mixed sols. The temperature of the endothermic and exothermic DTA peaks, corresponding to dehydration and crystallization, decreased with milling time. After milling the mixed sol for 5 min and heating to 823 K, the product was a single-phase PbTiO3. This suggests rapid homogenization and formation of lead titanate precursors during milling. The effects of milling were revealed to be much less when mixtures of dry and wet powders were used.

Mamoru Senna | K. Hamada | M. Senna | K. Hamada

[1] M. Senna. Incipient chemical interaction between fine particles under mechanical stress - a feasibility of producing advanced materials via mechanochemical routes , 1993 .

[2] M. Senna,et al. Mechanochemical synthesis of non-crystalline ZrTiO4 precursor from inhomogeneous mixed gels , 1995 .

[3] Kenji Hamada,et al. Characterization of CaCO3 ground by a Multiring Media Mill. , 1995 .

[4] M. Senna,et al. Effect of Preliminary Mechanical Treatment on the Microhomogenization during Heating of Hydrous Gels as Precursors for Lead Titanate , 1994 .

[5] J. Longo,et al. Synthesis of mixed-metal carbonates by grinding , 1989 .

[6] M. Senna,et al. Homogenization and Particle Size Reduction of PbTiO3 by Ball-Milling of Precursor Gels , 1994 .

[7] M. Senna,et al. Mechanochemical dehydration and amorphization of hydroxides of Ca, Mg and Al on grinding with and without SiO2 , 1993 .