Effects of porosity on the measured fracture energy of brittle materials

Although it is known that growing cracks will interact with pores, it is unclear whether the magnitude of this effect is sufficient to influence the fracture energy. To study this, experiments have been carried out where cracks have been grown through simple distributions of pores in poly(methyl methacrylate). These show that the applied force required to grow the crack between two pores can be greater than that required to grow the crack in the pore-free material. Direct observation during crack growth shows that this increase in applied force is associated with the crack front becoming curved. Based on these observations, the effect of equiaxed pores on the fracture energy of brittle materials has been quantitatively described. The analysis predicts how the relative fracture energy should be influenced by the pore volume fraction, and that it should be independent of the size of the pores or the fracture energy of the matrix. These predictions give good agreement with experimental measurements in different ceramic materials, in which the microstructure of the matrix surrounding the pores does not change with pore volume fraction.

[1]  J. Rödel,et al.  Evolution of Young's Modulus, Strength, and Microstructure during Liquid‐Phase Sintering , 2005 .

[2]  A. Horsewell,et al.  Fracture Resistance Measurement Method for in situ Observation of Crack Mechanisms , 2005 .

[3]  S. Kanzaki,et al.  Strain Tolerant Porous Silicon Nitride , 2005 .

[4]  J. Rödel,et al.  Evolution of Mechanical Properties of Porous Alumina during Free Sintering and Hot Pressing , 2004 .

[5]  S. Kanzaki,et al.  Microstructure and Mechanical Properties of Silicon Nitride Ceramics with Controlled Porosity , 2002 .

[6]  A. Boccaccini.  Fabrication, Microstructural Characterisation and Mechanical Properties of Glass Compacts Containing Controlled Porosity of Spheroidal Shape , 1999 .

[7]  A. Evans,et al.  Mechanical Properties of Partially Dense Alumina Produced from Powder Compacts , 1994 .

[8]  R. B. Poeppel,et al.  Dependence of ceramic fracture properties on porosity , 1993 .

[9]  T. Clyne,et al.  Fracture behaviour of ceramic laminates in bending—I. Modelling of crack propagation , 1993 .

[10]  A. Mukhopadhyay,et al.  Porosity dependence of strain of Si3N4 ceramics , 1988 .

[11]  E. Case,et al.  Room-temperature fracture energy of monoclinic Gd2O3 , 1981 .

[12]  J. Embury,et al.  Crack shape studies in brittle porous materials , 1977 .

[13]  M. Deighton.  Fracture of Brittle Solids , 1976 .

[14]  R. Bradt,et al.  Effects of Porosity on Fracture of Al2O3 , 1973 .

[15]  Anthony G. Evans,et al.  The strength of brittle materials containing second phase dispersions , 1972 .

[16]  K. Kendall,et al.  Surface energy and the contact of elastic solids , 1971, Proceedings of the Royal Society of London. A. Mathematical and Physical Sciences.

[17]  F. F. Lange,et al.  The interaction of a crack front with a second-phase dispersion , 1970 .

[18]  P. Arató.  Comment on “dependence of ceramics fracture properties on porosity” , 1996 .

[19]  I. Odler,et al.  Polymorphism and Hydration of Tricalcium Silicate Doped With ZnO , 1983 .

[20]  L. A. Simpson.  Effect of Microstructure on Measurements of Fracture Energy of Al2O3 , 1973 .

[21]  H. Tattersall,et al.  The work of fracture and its measurement in metals, ceramics and other materials , 1966 .

[22]  R. M. Spriggs,et al.  Strength-Grain Size-Porosity Relations in Alumina , 1965 .

[23]  A. A. Griffith.  The Phenomena of Rupture and Flow in Solids , 1921 .