20.1% Efficient Silicon Solar Cell With Aluminum Back Surface Field

We present a standard p<sup>+</sup>pn<sup>+</sup> solar cell device exhibiting a full-area aluminum back surface field (BSF) and a conversion efficiency of 20.1%. The front side features a shallow emitter which has been exposed to a short oxidation step and reduces the emitter dark saturation current density <i>j</i><sub>0</sub><i>e</i> to 160 fA/cm<sup>2</sup> on a textured surface. The front contact is formed by light-induced nickel and silver plating. Also, devices featuring screen-printed front contacts have been realized that reach a conversion efficiency of 19.8%. PC1D simulations are presented in order to extract the electronic parameters of the BSF. Therefore, external quantum efficiency and reflectance have been determined for modeling the internal quantum efficiency by adapting surface recombination and lifetime of the PC1D-simulated silicon device. As a result, a recombination velocity of <i>S</i><sub>BSF</sub> = 283 cm/s and a dark saturation current density of <i>j</i><sub>BSF</sub> = 274 fA/cm<sup>2</sup> in the Al BSF are determined. This results in an effective diffusion length <i>L</i><sub>eff</sub> = 1150 μm .

[1]  Yang Yang,et al.  Highly Predictive Modelling of Entire Si Solar Cells for Industrial Applications , 2009 .

[2]  A. Mette,et al.  Thermal oxidation for crystalline silicon solar cells exceeding 19% efficiency applying industrially feasible process technology , 2008 .

[3]  A. Cuevas,et al.  General parameterization of Auger recombination in crystalline silicon , 2002 .

[4]  Mark Kerr,et al.  Surface recombination velocity of phosphorus-diffused silicon solar cell emitters passivated with plasma enhanced chemical vapor deposited silicon nitride and thermal silicon oxide , 2001 .

[5]  A. Rohatgi,et al.  High‐efficiency (19%) screen‐printed textured cells on low‐resistivity float‐zone silicon with high sheet‐resistance emitters , 2006 .

[6]  Richard H. Bube,et al.  Fundamentals of solar cells , 1983 .

[7]  R. Preu,et al.  Selective Emitter by Laser Doping from Phosphosilicate Glass , 2009 .

[8]  S. Glunz,et al.  PROGRESS IN UNDERSTANDING THE CURRENT PATHS AND DEPOSITION MECHANISMS OF LIGHT- INDUCED PLATING AND IMPLICATIONS FOR THE PROCESS , 2009 .

[9]  R. Preu,et al.  Fundamental studies on the front contact formation resulting in a 21% efficiency silicon solar cell with printed rear and front contacts , 2010, 2010 35th IEEE Photovoltaic Specialists Conference.

[10]  D. A. Clugston,et al.  PC1D version 5: 32-bit solar cell modeling on personal computers , 1997, Conference Record of the Twenty Sixth IEEE Photovoltaic Specialists Conference - 1997.