Surface changes of corona-discharge-treated polyethylene films

Morphological and chemical changes of the surface of low-density polyethylene (LDPE), linear middle-density polyethylene (L-MDPE), and their 80/20 blend were studied by different techniques after corona-discharge treatment in air and subsequent annealing. The surface tension was determined by wetting; the roughness was measured by atomic force microscope (AFM), and the surface chemical composition was analyzed by X-ray photoelectron spectroscopy (XPS), whereas the low-molecular-mass fraction washed off by chloroform by FTIR. The surface tension of the films increases with the electrode current. The surface roughness depends primarily on the polymer type and is less affected by the corona treatment. At the initial stage of annealing, posttreatment-type oxidation and hydrophobic recovery are competing. The former is more pronounced in L-MDPE, the latter in LDPE. After annealing at 50°C for 160 days, hydrophobic recovery becomes predominant in each film studied, which is accompanied by significant smoothening of the surface. According to XPS and FTIR results, this is due to the migration of low-molecular-mass components (oligomers, oxidized polymer fractions, and additives) to the surface. © 2000 John Wiley & Sons, Inc. J Appl Polym Sci 76: 1529–1541, 2000

[1]  W. Sand,et al.  Microbially influenced corrosion visualized by atomic force microscopy , 1998 .

[2]  I. Bertóti,et al.  Oxidative damage and recovery of silicone rubber surfaces. I. X‐ray photoelectron spectroscopic study , 1994 .

[3]  C. Swanson,et al.  Meadowfoam monoenoic fatty acid amides as slip and antiblock agents in polyolefin film , 1993 .

[4]  D. Briggs,et al.  High Resolution XPS of Organic Polymers: The Scienta ESCA300 Database , 1992 .

[5]  D. Das-gupta.  Charge decay on polymer surfaces , 1989 .

[6]  D. Briggs,et al.  Adhesion to polyethylene and polypropylene , 1981 .

[7]  J. F. Carley,et al.  Corona-discharge treatment of polymeric films, II: Chemical studies , 1980 .

[8]  G. Socrates,et al.  Infrared Characteristic Group Frequencies , 1980 .

[9]  R. J. Bird,et al.  Energy calibration in electron spectroscopy and the re-determination of some reference electron binding energies , 1980 .

[10]  D. Briggs,et al.  Chemical basis of adhesion to electrical discharge treated polyethylene , 1979 .

[11]  D. Briggs,et al.  Surface modification of polyethylene by electrical discharge treatment and the mechanism of autoadhesion , 1978 .

[12]  D. K. Owens.  Mechanism of corona–induced self-adhesion of polyethylene film , 1975 .

[13]  D. Goring,et al.  Surface morphology of polyethylene after treatment in a corona discharge , 1971 .

[14]  K. Siegbahn.  ESCA : atomic, molecular and solid state structure studied by means of electron spectroscopy , 1967 .

[15]  Samuel Krimm,et al.  Infrared spectra of high polymers , 1960 .