Alkali activation of biomass fly ash–metakaolin blends

Abstract In this paper alkali activation of biomass fly ash – an industrial waste and biomass fly ash–metakaolin blends is investigated. Mixtures of biomass fly ash and commercially available metakaolin ARGICAL 1200 were used as solid components. Different molar volumes of NaOH and sodium silicate solutions were used for the preparation of alkali activators. The mechanical strength was determined after 10 days of curing. The concentration of alkali solution and the mix compositions were optimised for the preparation of mortar samples. The mineral and microstructural properties of the alkali activated binders were carried out by X-ray diffraction (XRD), Thermogravimetric/Differential thermal analysis (TG/DTA) and Scanning electron microscopy (SEM) methods. The mortar samples of biomass fly ashes gave a compressive strength of 18 MPa. The metakaolin incorporated samples showed a higher strength. The highest value was obtained for 40% metakaolin incorporated mortars for around 38 MPa. The biomass fly ash metakaolin blend is working well in the alkali activation application resulting in the contribution of both aluminosilicates and hydrated phases formation.

[1]  J. García,et al.  Lightweight concretes of activated metakaolin-fly ash binders, with blast furnace slag aggregates , 2010 .

[2]  Á. Palomo,et al.  Characterisation of fly ashes. Potential reactivity as alkaline cements , 2003 .

[3]  S. Alonso,et al.  Alkaline activation of metakaolin and calcium hydroxide mixtures: influence of temperature, activator concentration and solids ratio , 2001 .

[4]  Á. Palomo,et al.  Microstructure Development of Alkali-Activated Fly Ash Cement: A Descriptive Model , 2005 .

[5]  G. Mongelli,et al.  Fe concentration in palaeosols and in clayey marine sediments: two case studies in the Variscan basement of Sardinia (Italy) , 2008, Clay Minerals.

[6]  Larry L. Baxter,et al.  Biomass fly ash in concrete: Mixture proportioning and mechanical properties , 2008 .

[7]  P. S. Wiegand,et al.  Alternative management of pulp and paper industry solid wastes , 1994 .

[8]  J. Hower.  2003 International Ash Utilization Symposium , 2005 .

[9]  Larry L. Baxter,et al.  Comprehensive study of biomass fly ash in concrete: Strength, microscopy, kinetics and durability , 2007 .

[10]  J. Labrincha,et al.  Activation of mixtures of natural clay and glass cullet rejects , 2008 .

[11]  J. Deventer,et al.  The effect of ionic contaminants on the early-age properties of alkali-activated fly ash-based cements , 2002 .

[12]  Chai Jaturapitakkul,et al.  Compressive strength and degree of reaction of biomass- and fly ash-based geopolymer , 2010 .

[13]  Fernando Pacheco-Torgal,et al.  Alkali-activated binders: A review. Part 2. About materials and binders manufacture , 2008 .

[14]  R. Cloots,et al.  (Micro)-structural comparison between geopolymers, alkali-activated slag cement and Portland cement , 2006 .

[15]  Richard J Ball,et al.  Characterisation and use of biomass fly ash in cement-based materials. , 2009, Journal of hazardous materials.

[16]  Prinya Chindaprasirt,et al.  Preparation of fly ash and rice husk ash geopolymer , 2009 .

[17]  A. Fernández-Jiménez,et al.  Opc-fly ash cementitious systems: study of gel binders produced during alkaline hydration , 2007 .

[18]  J. Deventer,et al.  The coexistence of geopolymeric gel and calcium silicate hydrate at the early stage of alkaline activation , 2005 .

[19]  Hwai Chung Wu,et al.  New building materials from fly ash-based lightweight inorganic polymer , 2007 .

[20]  J.S.J. van Deventer,et al.  The characterisation of source materials in fly ash-based geopolymers , 2003 .