Replicated polymeric optical waveguide devices with large core connectable to plastic optical fiber using thermo-plastic and thermo-curable resins

Polymeric optical waveguide (POW) devices connectable to plastic optical fibers (POFs) fabricated by hot embossing using thermo-plastic resin are presented. Optical waveguides with large core sizes of 500 and 1000 /spl mu/m were fabricated, and a low propagation loss of /spl sim/ 0.2 dB/cm at 650 nm was achieved. A thick photoresist original master to obtain a stamper for hot embossing was fabricated by photolithography with a photoresist. Using photomasks with different patterns, POW device structures were fabricated. Two POW device structures are realized: one is a passive alignment structure and the other is a Y-branch-type POW. By passive alignment structure, POWs directly connected to POFs were realized, and the coupling loss from POF to POF through POW was measured to be 1.6 dB at an optimum core width of 900 /spl mu/m for 980-/spl mu/m core size POFs. Y-branch-type POWs with large core size of 1000 /spl mu/m, branching angle from 2/spl deg/ to 10/spl deg/, and branching top part radius of 200 /spl mu/m were fabricated. An output power ratio of 1:1 from each output port was realized. A compact-size Y-branch-type waveguide device was also proposed. POWs with high thermal resistance of more than 200/spl deg/C were also realized by hot replication using thermo-curable multifunctional methacrylate monomers.

[1]  S. Chuang,et al.  Wavelength conversion by dual-pump four-wave mixing in an integrated laser modulator , 2003, IEEE Photonics Technology Letters.

[2]  Andreas Neyer,et al.  Integration of polymer optical waveguides into printed circuit boards , 2000 .

[3]  Edgar Voges,et al.  Multimode polymeric waveguide devices fabricated by two-component injection moulding , 1997 .

[4]  J. Kobayashi,et al.  Fluorinated polyimide waveguides with low polarization-dependent loss and their applications to thermooptic switches , 1998 .

[5]  M. Kagami,et al.  Light-induced self-written polymeric optical waveguides for single-mode propagation and for optical interconnections , 2004, IEEE Photonics Technology Letters.

[6]  Oliver S. Roesch,et al.  High-performance low-cost fabrication method for integrated polymer optical devices , 1999, Optics & Photonics.

[7]  Way-Seen Wang,et al.  Compact Y-branch power splitter based on simplified coherent coupling , 2003 .

[8]  Paul M. Ferm,et al.  High volume manufacturing of polymer planar waveguides via UV embossing , 2000, SPIE Optics + Photonics.

[9]  Sang-Pil Han,et al.  Fabrication of large-core 1 x 16 optical power splitters in polymers using hot-embossing process , 2003 .

[10]  G.I. Stegeman,et al.  Efficient second harmonic generation in polymeric channel waveguides using modal dispersion , 1996, Summaries of papers presented at the Conference on Lasers and Electro-Optics.

[11]  Yasuko Yamada Maruo,et al.  Channel-optical-waveguide fabrication based on electron-beam irradiation of polyimides. , 1995, Applied optics.

[12]  Hirotaka Mizuno,et al.  Fabrication method of large-core polymeric optical waveguide through replication process using anisotropically etched silicon , 2004, SPIE OPTO.

[13]  Koji Enbutsu,et al.  Multimode Polymeric Optical Waveguides with High Thermal Stability Using UV Cured Epoxy Resins , 1997 .

[14]  O. Sugihara,et al.  Low-loss polymeric optical waveguides with large cores fabricated by hot embossing. , 2003, Optics letters.

[15]  R. B. Hooker,et al.  Tapered polymer single-mode waveguides for mode transformation , 1999 .

[16]  A. Neyer,et al.  Low loss polymer waveguides at 1300 and 1550 nm using halogenated acrylates , 1996 .

[17]  Jae-Wook Kang,et al.  Simple and Low Cost Fabrication of Thermally Stable Polymeric Multimode Waveguides using a UV-curable Epoxy , 2003 .

[18]  Hiroshi Ito,et al.  Light-induced self-written three-dimensional optical waveguide , 2001 .

[19]  M Kagami,et al.  Simultaneous fabrication of optical channel waveguides and out-of-plane branching mirrors from a polymeric slab structure. , 1997, Applied optics.

[20]  M Kagami,et al.  Fabrication of large-core, high-Δ optical waveguides in polymers. , 1995, Applied optics.