论文信息 - PbS and HgTe quantum dots for SW IR devices

PbS and HgTe quantum dots for SW IR devices

HgTe and PbS colloidal quantum dots (CQD) with first excitonic absorption peak of about 2 μm and shorter (down to about 1 μm) have been synthesized and characterized. The synthesized CQDs were characterized using FTIR spectroscopy and TEM technique. The nanomaterials were tested for photo-electrical properties with photoconductive (PC) devices. The devices were fabricated by drop-casting a suspension of the CQDs on the fanout, followed by solid state ligand exchange (SSLE) process, and then spectral and electrical photoresponse of the device were measured. The SSLE process was evaluated thru absorption spectra of test samples. The device fabrication parameters were the number of deposited layers, the thickness of individual layers, the type of the substituting ligand, and the ligand exchange duration. For selected devices external quantum efficiency (EQE) was also determined.

[1] B. Streetman. Solid state electronic devices , 1972 .

[2] P. Guyot-Sionnest,et al. Synthesis of colloidal HgTe quantum dots for narrow mid-IR emission and detection. , 2011, Journal of the American Chemical Society.

[3] Philippe Guyot-Sionnest,et al. Optical properties of HgTe colloidal quantum dots , 2012, Nanotechnology.

[4] F. Wise,et al. Electronic structure and optical properties of PbS and PbSe quantum dots , 1997 .

[5] Holger T. Grahn. Introduction To Semiconductor Physics , 1999 .

[6] Cherie R. Kagan,et al. Building devices from colloidal quantum dots , 2016, Science.

[7] I. Moreels,et al. Size-dependent optical properties of colloidal PbS quantum dots. , 2009, ACS nano.

[8] S. Trivedi,et al. HgTe Quantum Dots for Near-, Mid-, and Long-Wavelength IR Devices , 2017, Journal of Electronic Materials.

[9] Philippe Guyot-Sionnest,et al. Mercury telluride colloidal quantum dots: electronic structure, size-dependent spectra, and photocurrent detection up to 12 μm. , 2014, ACS nano.