Field emission properties of amorphous GaN ultrathin films fabricated by pulsed laser deposition

Amorphous gallium nitride (a-GaN) films with thicknesses of 5 and 300 nm are deposited on n-Si (100) substrates by pulsed laser deposition (PLD), and their field emission (FE) properties are studied. It shows that compared with thicker (300 nm) a-GaN film, better FE performance is obtained on ultrathin (5 nm) a-GaN film with a threshold field of 0.78 V/µm, which is the lowest value ever reported. Furthermore, the current density reaches 42 mA/cm2 when the applied field is 3.72 V/µm. These experimental results unambiguously confirm Binh’s theoretical analysis (Binh et al. Phys Rev Lett, 2000, 85(4): 864–867) that the FE performance would be prominently enhanced with the coating of an ultra-thin wide band-gap semiconductor film.

[1]  K. Hiramatsu,et al.  Formation of GaN Self-Organized Nanotips by Reactive Ion Etching , 2001 .

[2]  Ziqiang Zhu,et al.  Field emission from GaN nanobelts with herringbone morphology , 2004 .

[3]  Enge Wang,et al.  Vacuum gap dependence of field electron emission properties of large area multi-walled carbon nanotube films , 2001 .

[4]  C. S. Chen,et al.  The effect of nitrogen pressure on the two-step method deposition of GaN films , 2006 .

[5]  Jitsuo Ohta,et al.  Room temperature epitaxial growth of m-plane GaN on lattice-matched ZnO substrates , 2007 .

[6]  Yanwu Zhu,et al.  Field emission enhancement from patterned gallium nitride nanowires , 2007 .

[7]  Huigao Duan,et al.  Field emission from amorphous GaN deposited on Si by dc sputtering , 2006 .

[8]  Teresa Monteiro,et al.  Characterisation of GaN films grown on sapphire by low-temperature cyclic pulsed laser deposition/nitrogen rf plasma , 2003 .

[9]  Jiaxin Li,et al.  Enhanced electron field emission from oriented AlN films , 2006 .

[10]  Hui Yan,et al.  Band bending mechanism for field emission in wide-band gap semiconductors , 2002 .

[11]  Shigehiko Hasegawa,et al.  Electron field emission from GaN nanorod films grown on Si substrates with native silicon oxides , 2005 .

[12]  D. Late,et al.  Field emission from a-GaN films deposited on Si (100) , 2004 .

[13]  Jun Chen,et al.  Effect of structural parameter on field emission properties of semiconducting copper sulphide nanowire films , 2003 .

[14]  Hideyoshi Horie,et al.  Growth of a-plane GaN on lattice-matched ZnO substrates using a room-temperature buffer layer , 2007 .

[15]  Cheng Yang,et al.  Annealing of GaN/ZnO/Si Films Deposited by Pulsed Laser Deposition , 2007 .

[16]  Binh,et al.  New mechanism for electron emission from planar cold cathodes: the solid-state field-controlled electron emitter , 2000, Physical review letters.

[17]  Xiaojun Pan,et al.  The influence of H2 plasma treatment on the field emission of amorphous GaN film , 2006 .

[18]  Shigehiko Hasegawa,et al.  Polycrystalline GaN for light emitter and field electron emitter applications , 2005 .

[19]  R. Fowler,et al.  Electron Emission in Intense Electric Fields , 1928 .

[20]  Sungho Jin,et al.  Defect‐enhanced electron field emission from chemical vapor deposited diamond , 1995 .

[21]  Y. Bando,et al.  Excellent field-emission properties of P-doped GaN nanowires. , 2005, The journal of physical chemistry. B.

[22]  Timothy S. Fisher,et al.  Field emission from GaN and (Al,Ga)N∕GaN nanorod heterostructures , 2007 .

[23]  Hans L. Hartnagel,et al.  Field emission from quantum size GaN structures , 2003 .