In vivo corrosion and corrosion protection of magnesium alloy LAE442.

The aim of this study was to investigate whether the extruded magnesium alloy LAE442 reacts in vivo with an appropriate host response and to investigate how an additional magnesium fluoride (MgF(2)) coating influences the in vivo corrosion rate. Forty cylinders were machined from extruded LAE442 and 20 of these were coated additionally with MgF(2) and implanted into the medial femur condyle of adult rabbits. Synchrotron-radiation-based X-ray computed micro-tomography (SRmicroCT) was used to quantitatively analyse corrosion non-destructively in vivo and comparisons were made to magnesium degradation rates based on area measurements of the remaining metal on uncalcified sections. Blood concentrations of the alloying elements were measured below toxicological limits. The MgF(2) layer was no longer detected after 4 weeks of implantation by particle-induced gamma emission, and the MgF(2) coating reduced the blood content of alloying elements during the first 6 weeks of implantation with no elevated fluoride concentration in the adjacent bone. Histopathological examinations of liver showed in 9 out of 40 cases minimal infiltrations of heterophil granulocytes of unknown origin (5 LAE442, 4 LAE442+MgF(2)). The kidneys were mainly regular in structure. The synovial tissue showed a granular cell infiltration as a temporary observation in the LAE442+MgF(2) group after 2 weeks. No subcutaneous gas cavities were observed clinically and on postoperative X-rays in all animals. All specimens were scanned by SRmicroCT at 2, 4, 6 and 12 weeks postoperatively before uncalcified sections were performed. All magnesium implants have been observed in direct bone contact and without a fibrous capsule. Localized pitting corrosion occurred in coated and uncoated magnesium implants. This study shows that the extruded magnesium alloy LAE442 provides low corrosion rates and reacts in vivo with an acceptable host response. The in vivo corrosion rate can be further reduced by additional MgF(2) coating.

[1]  U. Bonse,et al.  3D computed X-ray tomography of human cancellous bone at 8 microns spatial and 10(-4) energy resolution. , 1994, Bone and mineral.

[2]  Frank Witte,et al.  Degradable biomaterials based on magnesium corrosion , 2008 .

[3]  M. Störmer,et al.  Biodegradable magnesium-hydroxyapatite metal matrix composites. , 2007, Biomaterials.

[4]  W. Ziegler,et al.  Magnesium und seine Legierungen , 1939 .

[5]  R. Bertholf,et al.  Trace metals and degenerative diseases of the skeleton. , 2009, Acta Pharmacologica et Toxicologica.

[6]  E. Mcbride,et al.  ABSORBABLE METAL IN BONE SURGERY: A FURTHER REPORT ON THE USE OF MAGNESIUM ALLOYS , 1938 .

[7]  Gabor T. Herman,et al.  Image reconstruction from projections : implementation and applications , 1979 .

[8]  Ke Yang,et al.  In vitro corrosion behaviour of Mg alloys in a phosphate buffered solution for bone implant application , 2008, Journal of materials science. Materials in medicine.

[9]  J. Prendergast,et al.  Chemical gas gangrene from metallic magnesium , 1942 .

[10]  T. Luckey,et al.  Lanthanide markers in a single sample for nutrient studies in humans. , 1979, The Journal of nutrition.

[11]  H. Haferkamp,et al.  In vivo corrosion of four magnesium alloys and the associated bone response. , 2005, Biomaterials.

[12]  O. Duygulu,et al.  The effects of magnesium particles in posterolateral spinal fusion: an experimental in vivo study in a sheep model. , 2007, Journal of neurosurgery. Spine.

[13]  Frank Witte,et al.  In vitro and in vivo corrosion measurements of magnesium alloys. , 2006, Biomaterials.

[14]  Ulrich Bonse,et al.  X-ray computed microtomography (μCT) using synchrotron radiation (SR) , 1996 .

[15]  P. Thurner,et al.  Comparison of microfocus- and synchrotron X-ray tomography for the analysis of osteointegration around Ti6Al4V implants. , 2004, European cells & materials.

[16]  Felix Beckmann,et al.  Osteoconductive modifications of Ti-implants in a goat defect model: characterization of bone growth with SR muCT and histology. , 2005, Biomaterials.

[17]  Andreas Schreyer,et al.  Characterization of polyurethane scaffolds using synchrotron radiation based computed microtomography , 2004, SPIE Optics + Photonics.

[18]  Jef A. Helsen,et al.  Metals as Biomaterials , 1998 .

[19]  F. Witte,et al.  Determination of concentration gradients in bone tissue generated by a biologically degradable magnesium implant , 2009 .

[20]  G. Song,et al.  Corrosion mechanisms of magnesium alloys , 1999 .

[21]  Edward Ghali,et al.  Magnesium and Magnesium Alloys , 2011 .

[22]  J. Kruger,et al.  Corrosion of magnesium , 1993 .

[23]  Ke Yang,et al.  In vivo evaluation of biodegradable magnesium alloy bone implant in the first 6 months implantation. , 2009, Journal of biomedical materials research. Part A.

[24]  K. P. Dubois,et al.  THE ACUTE MAMMALIAN TOXICITY OF RARE EARTH NITRATES AND OXIDES. , 1963, Toxicology and applied pharmacology.

[25]  Ke Yang,et al.  In vivo corrosion behavior of Mg-Mn-Zn alloy for bone implant application. , 2007, Journal of biomedical materials research. Part A.

[26]  E. Willbold,et al.  Biodegradable magnesium scaffolds: Part 1: appropriate inflammatory response. , 2007, Journal of biomedical materials research. Part A.