Modification of MELCOR for severe accident analysis of candidate accident tolerant cladding materials

Abstract A number of materials are currently under development as candidate accident tolerant fuel and cladding for application in the current fleet of commercial light water reactors (LWRs). The safe, reliable and economic operation of the nation’s nuclear power reactor fleet has always been a top priority for the nuclear industry. Continual improvement of technology, including advanced materials and nuclear fuels, remains central to the industry’s success. Enhancing the accident tolerance of light water reactors became a topic of serious discussion following the 2011 Great East Japan Earthquake, resulting tsunami, and subsequent damage to the Fukushima Daiichi nuclear power plant complex. The overall goal for the development of accident tolerant fuel (ATF) systems for LWRs is to identify alternative fuel system technologies to further enhance the safety, competitiveness, and economics of commercial nuclear power. Designed for use in the current fleet of commercial LWRs, or in reactor concepts with design certifications (GEN-III+), to achieve their goal enhanced ATF must endure loss of active cooling in the reactor core for a considerably longer period of time than the current fuel system, while maintaining or improving performance during normal operation. Many available nuclear fuel performance analysis tools are specifically developed for the current UO2–Zirconium alloy fuel system. The MELCOR severe-accident analysis code, under development at the Sandia National Laboratory in New Mexico (SNL-NM) for the US Nuclear Regulatory Commission (NRC), is one of these tools. This paper describes modifications made to a version of the MELCOR code by the Idaho National Laboratory (INL) that allows its application to alternate fuel-cladding systems. Preliminary analysis results are presented in this paper for candidate silicon carbide and FeCrAl cladding concepts.

[1]  Dennis S. Fox,et al.  Oxidation Behavior of Chemically-Vapor-Deposited Silicon Carbide and Silicon Nitride from 1200° to 1600°C , 2005 .

[2]  Kurt A. Terrani,et al.  Silicon Carbide Oxidation in Steam up to 2 MPa , 2014 .

[3]  James L. Smialek,et al.  SiC Recession Caused by SiO2 Scale Volatility under Combustion Conditions: I, Experimental Results and Empirical Model , 1999 .

[4]  Akihiko Hashimoto,et al.  The effect of H2O gas on volatilities of planet-forming major elements: I. Experimental determination of thermodynamic properties of Ca-, Al-, and Si-hydroxide gas molecules and its application to the solar nebula , 1992 .

[5]  Claudio Francesco Badini,et al.  Oxidation of FeCrAl alloy: influence of temperature and atmosphere on scale growth rate and mechanism , 2001 .

[6]  Kurt A. Terrani,et al.  High temperature oxidation of fuel cladding candidate materials in steam–hydrogen environments , 2013 .

[7]  Karren L. More,et al.  Effects of High Water‐Vapor Pressure on Oxidation of Silicon Carbide at 1200°C , 2003 .

[8]  Randall O. Gauntt,et al.  MELCOR 1.8.5 Simulation of TMI-2 Phase 2 With an Enhanced 2-Dimensional In-Vessel Natural Circulation Model , 2002 .

[9]  Robert E. Wilson,et al.  Fundamentals of momentum, heat, and mass transfer , 1969 .

[10]  E. Opila,et al.  Oxidation and Volatilization of Silica-Formers in Water Vapor , 2013 .

[11]  Shannon M. Bragg-Sitton,et al.  SiC MODIFICATIONS TO MELCOR FOR SEVERE ACCIDENT ANALYSIS APPLICATIONS , 2013 .

[12]  P. Ho,et al.  Theoretical Study of the Thermochemistry of Molecules in the SiO-H System , 2001 .

[13]  Kurt A. Terrani,et al.  Development and property evaluation of nuclear grade wrought FeCrAl fuel cladding for light water reactors , 2015 .

[14]  R. C. Weast.  Handbook of chemistry and physics , 1973 .