Electrochemical Fabrication of Multi-Nanolayers

The fabrication of multi-nanolayer structures can in some cases be achieved electrochemically if, for example, the plating current density has a significant effect on the deposit composition or if reverse plating changes the composition. Moreover, the realization of a multi-nanolayer structure can also crucially affect the properties of the material. This chapter will look at one material system in which both of the above apply, namely, amorphous Co-P. When produced using conventional DC plating, amorphous Co-P tends to exhibit perpendicular magnetic anisotropy and hence very low permeability and somewhat high coercivity. This limits the usefulness of the material as a magnetic core for power conversion applications which require low coercivity, high saturation magnetization, high permeability, high anisotropy field, and high resistivity. Riveiro et al. used pulse reverse plating to fabricate multilayers of alternate magnetic and nonmagnetic materials. With the thickness of the magnetic layers at around 30 nm, they were able to achieve in-plane anisotropy and low coercivity 8 A m . This chapter will describe the early work and a selection of subsequent research on multi-nanolayers of amorphous Co-P, e.g., Perez et al., who used pulse plating, and McCloskey et al., who improved the saturation magnetization and thermal stability of the material.

[1]  C. Aroca,et al.  Electrodeposited amorphous CoP multilayers with high permeability , 2000 .

[2]  S. Djokić Electrodeposition of Amorphous Alloys Based on the Iron Group of Metals , 1999 .

[3]  SOFT-MAGNETIC FLUXGUIDE MATERIALS , 1998 .

[4]  C. Tsang,et al.  Gigabit density recording using dual-element MR/Inductive heads on thin-film disks , 1990, International Conference on Magnetics.

[5]  Mihail C Roco,et al.  Nanoelectronics: An International Perspective [Point of View] , 2011 .

[7]  A. Brenner,et al.  Electrodeposition of alloys of phosphorus with nickel or cobalt , 1950 .

[8]  J. Celis,et al.  Microstructural investigation of Co-P by TEM , 2004 .

[9]  Michael A. Wilson,et al.  Nanotechnology: Basic Science and Emerging Technologies , 2002 .

[10]  G. Rivero,et al.  Multilayered magnetic amorphous Co-P films , 1981 .

[11]  David S. Lashmore,et al.  Growth and characterization of electrodeposited Cu/Cu-Ni-Co alloy superlattices , 1993 .

[12]  M. Sánchez,et al.  Electrodeposited amorphous Co-P alloys with variable magnetic anisotropy , 1981 .

[13]  Walther Schwarzacher,et al.  Magnetoresistance in electrodeposited Ni-Fe-Cu/Cu multilayers , 1995 .

[14]  G. Ali Mansoori,et al.  Principles of nanotechnology , 2005 .

[15]  Stuart A. Wolf,et al.  Spintronics : A Spin-Based Electronics Vision for the Future , 2009 .

[16]  R. S. Timsit,et al.  Structure of composition-modulated Cu/Ni thin films prepared by electrodeposition , 1989 .

[17]  C. Aroca,et al.  Planar fluxgate sensor with an electrodeposited amorphous core , 2004 .

[18]  C. Tsang,et al.  High Performance Write Head Using NiFe 45/55 , 1997 .

[19]  X. Yi,et al.  Planarization of CMOS ROIC dies for uncooled detectors , 2006 .

[20]  G.E. Moore,et al.  Cramming More Components Onto Integrated Circuits , 1998, Proceedings of the IEEE.

[21]  D. Landolt Electrochemical and materials science aspects of alloy deposition , 1994 .

[22]  M. Schlesinger,et al.  Electrochemically Layered Copper‐Nickel Nanocomposites with Enhanced Hardness , 1994 .

[23]  J. Riveiro,et al.  Magnetic anisotropy of electrodeposited Co--P amorphous alloys , 1980 .

[24]  M. Sánchez,et al.  Magnetic domains in multilayered amorphous Co-P alloys , 1982 .

[25]  A. Brenner,et al.  Electrodeposition of Alloys , 1964 .

[26]  K. D. Bird,et al.  Giant Magnetoresistance in Electrodeposited Ni/Cu and Co/Cu Multilayers , 1995 .

[27]  D. Gardner,et al.  Electrodeposited amorphous Co–P based alloy with improved thermal stability , 2010 .

[28]  M. Schlesinger,et al.  1. Fundamental Considerations , 2011 .