Effect of silanization on shear bond strength between high translucency zirconia and resin cement

Aim: This in-viro study aimed to evaluate and compare the shear bond strength of resin cement with high translucency zirconia with silane coupling agents and bonding agent separately (Group3), bonding agent containing silane (Group 2) and bonding agent which does not have silane (Group 1). Materials and Methods: The study was conducted by using the high translucency zirconia blanks along with the CAD-CAM equipments. After sintering the specimens according to manufacturer’s instructions surface modifications, bonding procedures and evaluation of bond strength was performed. Bond strength of the samples was tested using universal testing machine. The results were analyzed statistically using descriptive analysis. Results: The mean shear bond strength obtained for group 1, group 2 and group 3 was 17.97, 22.01, 28.87MPA respectively. The SBS of group 3 was significantly higher than the other two groups as the surface of zirconia was treated with both Silane and Silane-containing universal adhesive. Conclusion: The null hypothesis was rejected. Within the limitations of the study, it was concluded that the shear bond strength between resin cement and high translucency zirconia was highest when treated with bonding agent (universal adhesive) and silane coupling agent separately after air particle abrasion.

[1]  Özay Önöral,et al.  How will surface conditioning methods influence the translucency and color properties of CAD-CAM resin-matrix ceramics with different thicknesses? , 2020, Journal of esthetic and restorative dentistry : official publication of the American Academy of Esthetic Dentistry ... [et al.].

[2]  N. Ruse,et al.  Fracture Toughness, Flexural Strength and Flexural Modulus of New CAD/CAM Resin Composite Blocks. , 2019, Journal of prosthodontics : official journal of the American College of Prosthodontists.

[3]  R. Khan,et al.  Effect of universal adhesives on microtensile bond strength to hybrid ceramic , 2019, BMC Oral Health.

[4]  Markus B Blatz,et al.  The Current State of Chairside Digital Dentistry and Materials. , 2019, Dental clinics of North America.

[5]  A. Çulhaoglu,et al.  Surface Roughness of Ceramic-Resin Composites After Femtosecond Laser Irradiation, Sandblasting or Acid Etching and Their Bond Strength With and Without Silanization to a Resin Cement. , 2019, Operative dentistry.

[6]  Chen Chen,et al.  Effect of tribochemical silica coating or multipurpose products on bonding performance of a CAD/CAM resin-based material. , 2019, Journal of the mechanical behavior of biomedical materials.

[7]  Sevcan Kurtulmus-Yilmaz,et al.  The Effect of Surface Treatments on the Mechanical and Optical Behaviors of CAD/CAM Restorative Materials , 2019, Journal of prosthodontics : official journal of the American College of Prosthodontists.

[8]  C. Baydemır,et al.  Microtensile Bond Strength of CAD/CAM Resin Blocks to Dual‐Cure Adhesive Cement: The Effect of Different Sandblasting Procedures , 2019, Journal of prosthodontics : official journal of the American College of Prosthodontists.

[9]  H. Ikeda,et al.  Correlation between microstructure of CAD/CAM composites and the silanization effect on adhesive bonding. , 2019, Journal of the mechanical behavior of biomedical materials.

[10]  R. Weiger,et al.  Influence of Pretreatment Methods on the Adhesion of Composite and Polymer Infiltrated Ceramic CAD-CAM Blocks. , 2019, The journal of adhesive dentistry.

[11]  U. S. Buyukkaplan,et al.  Effect of Different Surface Treatments on Bond Strength of Resin Cement to a CAD/CAM Restorative Material , 2019, Journal of prosthodontics : official journal of the American College of Prosthodontists.

[12]  Esra Cengiz-Yanardag,et al.  Effect of Different Surface Treatment Methods on Micro-Shear Bond Strength of CAD-CAM Restorative Materials to Resin Cement. , 2019, Journal of Adhesion Science and Technology.

[13]  D. Dede,et al.  Shear Bond Strength of Nanohybrid Composite to the Resin Matrix Ceramics After Different Surface Treatments. , 2018, Photomedicine and laser surgery.

[14]  M. Ulusoy,et al.  Optical properties of contemporary monolithic CAD‐CAM restorative materials at different thicknesses , 2018, Journal of esthetic and restorative dentistry : official publication of the American Academy of Esthetic Dentistry ... [et al.].

[15]  Jian Yu,et al.  Acidic pH weakens the bonding effectiveness of silane contained in universal adhesives. , 2018, Dental materials : official publication of the Academy of Dental Materials.

[16]  Daniel Edelhoff,et al.  Bonding to new CAD/CAM resin composites: influence of air abrasion and conditioning agents as pretreatment strategy , 2018, Clinical Oral Investigations.

[17]  T. Sawase,et al.  Effects of three silane primers and five adhesive agents on the bond strength of composite material for a computer-aided design and manufacturing system , 2018, Journal of applied oral science : revista FOB.

[18]  Vanessa Bernasconi Stange,et al.  Hybrid Ceramics in Dentistry: A Literature Review , 2018 .

[19]  J. Matinlinna,et al.  Silane adhesion mechanism in dental applications and surface treatments: A review. , 2018, Dental materials : official publication of the Academy of Dental Materials.

[20]  A. Mainjot,et al.  Bonding to CAD-CAM Composites: An Interfacial Fracture Toughness Approach , 2018, Journal of dental research.

[21]  Hualing Sun,et al.  Effect of silane pretreatment on the immediate bonding of universal adhesives to computer‐aided design/computer‐aided manufacturing lithium disilicate glass ceramics , 2017, European journal of oral sciences.

[22]  B. Van Meerbeek,et al.  Sandblasting may damage the surface of composite CAD-CAM blocks. , 2017, Dental materials : official publication of the Academy of Dental Materials.

[23]  J. Fischer,et al.  Efficacy of a Universal Adhesive in the Bond Strength of Composite Cements to Polymer-infiltrated Ceramic. , 2017, The journal of adhesive dentistry.

[24]  T. Sawase,et al.  Effects of tributylborane-activated adhesive and two silane agents on bonding computer-aided design and manufacturing (CAD/CAM) resin composite , 2017, Odontology.

[25]  Y. Makita,et al.  Effectiveness and stability of silane coupling agent incorporated in 'universal' adhesives. , 2016, Dental materials : official publication of the Academy of Dental Materials.

[26]  A. Mainjot.  Recent advances in composite CAD/CAM blocks. , 2016, The international journal of esthetic dentistry.

[27]  V. Thompson,et al.  A new classification system for all-ceramic and ceramic-like restorative materials. , 2016, The International journal of prosthodontics.

[28]  D. Nathanson,et al.  Mechanical properties of resin-ceramic CAD/CAM restorative materials. , 2015, The Journal of prosthetic dentistry.

[29]  D. Edelhoff,et al.  Bonding between CAD/CAM resin and resin composite cements dependent on bonding agents: three different in vitro test methods , 2015, Clinical Oral Investigations.

[30]  S. Elsaka.  Bond strength of novel CAD/CAM restorative materials to self-adhesive resin cement: the effect of surface treatments. , 2014, The journal of adhesive dentistry.

[31]  M. Blatz,et al.  Resin bond to indirect composite and new ceramic/polymer materials: a review of the literature. , 2014, Journal of esthetic and restorative dentistry : official publication of the American Academy of Esthetic Dentistry ... [et al.].

[32]  Jukka Pekka Matinlinna,et al.  Ceramic dental biomaterials and CAD/CAM technology: state of the art. , 2014, Journal of prosthodontic research.

[33]  A. Reis,et al.  The effect of the loading method and cross-head speed on resin–dentin microshear bond strength , 2014 .

[34]  K. Tsubota,et al.  Important compositional characteristics in the clinical use of adhesive systems. , 2014, Journal of oral science.

[35]  L. Valandro,et al.  Effect of post-silanization heat treatments of silanized feldspathic ceramic on adhesion to resin cement. , 2013, The journal of adhesive dentistry.

[36]  S. L. Santiago,et al.  Effect of surface pretreatments on the microtensile bond strength of lithium-disilicate ceramic repaired with composite resin. , 2013, Brazilian dental journal.

[37]  V. Migonney,et al.  Resin composite blocks via high-pressure high-temperature polymerization. , 2012, Dental materials : official publication of the Academy of Dental Materials.

[38]  M. Bottino,et al.  Surface characterization of feldspathic ceramic using ATR FT-IR and ellipsometry after various silanization protocols. , 2012, Dental materials : official publication of the Academy of Dental Materials.

[39]  M. Scharnberg,et al.  Influence of Contamination on Zirconia Ceramic Bonding , 2007, Journal of dental research.

[40]  M. Kılıçarslan,et al.  Effect of zirconium-oxide ceramic surface treatments on the bond strength to adhesive resin. , 2006, The Journal of prosthetic dentistry.

[41]  J. C. Pereira,et al.  Surface treatment protocols in the cementation process of ceramic and laboratory-processed composite restorations: a literature review. , 2005, Journal of esthetic and restorative dentistry : official publication of the American Academy of Esthetic Dentistry ... [et al.].

[42]  L. C. Vieira,et al.  Effect of different ceramic surface treatments on resin microtensile bond strength. , 2004, Journal of prosthodontics : official journal of the American College of Prosthodontists.

[43]  P. Vallittu,et al.  Effect of surface conditioning methods on the bond strength of luting cement to ceramics. , 2003, Dental materials : official publication of the Academy of Dental Materials.

[44]  Markus B Blatz,et al.  Resin-ceramic bonding: a review of the literature. , 2003, The Journal of prosthetic dentistry.

[45]  K. Söderholm,et al.  Molecular Orientation of Silane at the Surface of Colloidal Silica , 1993, Journal of dental research.