Dispersion and Setting of Powder Suspensions in Concentrated Aqueous Urea Solutions for the Preparation of Porous Alumina Ceramics with Aligned Pores

Highly concentrated alumina powder suspensions have been prepared in aqueous urea solutions of concentrations in the range 200–360 g/100 mL using an ammonium poly(acrylate) dispersant at 80°C. The dispersant concentration for the suspension viscosity minimum in the urea solutions is higher than that in water due to the higher processing temperature. The urea solutions having higher dielectric constant than that of water offer higher interparticle potential that resulted in better dispersion of the powder as evidenced from the lower viscosity and yield stress of the suspensions. The decrease in temperature increased the suspension viscosity and the suspension formed a strong gel when cooled to room temperature due to the crystallization of urea. The minimum urea solution concentration for a 55 vol% alumina suspension to form a dimensionally stable gel is 240 g/100 mL. The compressive strength and Young's modulus of the gels increased with the increase in urea solution concentration. The alumina ceramics prepared by the urea removal followed by sintering at 1500°C had porosity in the range 28–36 vol% with the rectangular rod-shaped aligned pores.

[1]  Michael J. Hoffmann,et al.  Processing and Elastic Property Characterization of Porous SiC Preform for Interpenetrating Metal/Ceramic Composites , 2012 .

[2]  Hyoun‐Ee Kim,et al.  Porous alumina ceramics with highly aligned pores by heat-treating extruded alumina/camphene body at temperature near its solidification point , 2012 .

[3]  W. Pabst,et al.  Process control and optimized preparation of porous alumina ceramics by starch consolidation casting , 2011 .

[4]  Hongjie Wang,et al.  Porous Si3N4 Fabricated by Phase Separation Method Using Benzoic Acid as Pore-Forming Agent , 2011 .

[5]  Rui Guo,et al.  Piezoelectric Properties of the 1–3 Type Porous Lead Zirconate Titanate Ceramics , 2011 .

[6]  M. Fuji,et al.  Opportunities of porous ceramics fabricated by gelcasting in mitigating environmental issues , 2009 .

[7]  David S. Smith,et al.  Thermal conductivity of porous alumina ceramics prepared using starch as a pore-forming agent , 2009 .

[8]  T. Graule,et al.  Homogeneous Ni-P/Al(2)O(3) nanocomposite coatings from stable dispersions in electroless nickel baths. , 2008, Journal of colloid and interface science.

[9]  L. Bergström,et al.  Gas-filled microspheres as an expandable sacrificial template for direct casting of complex-shaped macroporous ceramics , 2008 .

[10]  T. Graule,et al.  Interactions and dispersion stability of aluminum oxide colloidal particles in electroless nickel solutions in the presence of comb polyelectrolytes. , 2008, Journal of colloid and interface science.

[11]  Hyoun‐Ee Kim,et al.  Aligned porous alumina ceramics with high compressive strengths for bone tissue engineering , 2008 .

[12]  S. Deville.  Freeze‐Casting of Porous Ceramics: A Review of Current Achievements and Issues , 2008, 1710.04201.

[13]  Hyoun‐Ee Kim,et al.  Freezing Dilute Ceramic/Camphene Slurry for Ultra‐High Porosity Ceramics with Completely Interconnected Pore Networks , 2006 .

[14]  T. Moritz,et al.  Ceramic Bodies with Complex Geometries and Ceramic Shells by Freeze Casting Using Ice as Mold Material , 2006 .

[15]  André R. Studart,et al.  Processing Routes to Macroporous Ceramics: A Review , 2006 .

[16]  X. Miao,et al.  Porous alumina ceramics prepared by slurry infiltration of expanded polystyrene beads , 2005 .

[17]  Byong-Taek Lee,et al.  Fabrication of a Continuously Oriented Porous Al2O3 Body and Its In Vitro Study , 2005 .

[18]  J. Halloran,et al.  Porous Ceramic Bodies with Interconnected Pore Channels by a Novel Freeze Casting Technique , 2005 .

[19]  R. Glass,et al.  Effects of the Use of Pore Formers on Performance of an Anode supported Solid Oxide Fuel Cell , 2005 .

[20]  J. Halloran,et al.  Room-Temperature Freeze Casting for Ceramics with Nonaqueous Sublimable Vehicles in the Naphthalene–Camphor Eutectic System , 2005 .

[21]  Wolfgang M. Sigmund,et al.  Novel Powder-Processing Methods for Advanced Ceramics , 2004 .

[22]  L. Gauckler,et al.  Mechanical Properties of Coagulated Wet Particle Networks with Alkali‐Swellable Thickeners , 2004 .

[23]  J. Lewis.  Colloidal Processing of Ceramics , 2004 .

[24]  Y. Sakka,et al.  Fabrication of Macroporous Alumina with Tailored Porosity , 2003 .

[25]  S. Kanzaki,et al.  Synthesis of Porous Silicon Nitride with Unidirectionally Aligned Channels Using Freeze‐Drying Process , 2002 .

[26]  M. M. Garcia-Mira,et al.  pH corrections in chemical denaturant solutions. , 2002, Analytical biochemistry.

[27]  F. S. Ortega,et al.  Properties of Highly Porous Hydroxyapatite Obtained by the Gelcasting of Foams , 2000 .

[28]  P. M. Biesheuvel,et al.  Design of ceramic membrane supports: permeability, tensile strength and stress , 1999 .

[29]  J. P. Chen,et al.  Thermal Decomposition of Urea and Urea Derivatives by Simultaneous TG/(DTA)/MS , 1998 .

[30]  N. Minh.  Ceramic Fuel Cells , 1993 .

[31]  J. Cesarano,et al.  Processing of Highly Concentrated Aqueous α‐Alumina Suspensions Stabilized with Polyelectrolytes , 1988 .

[32]  F. Miller,et al.  The Solubility of Urea in Water. The Heat of Fusion of Urea , 1934 .

[33]  J. Wyman.  Dielectric Constants: Ethanol—Diethyl Ether and Urea—Water Solutions between 0 and 50° , 1933 .

[34]  K. Ryan,et al.  Controlled semiconductor nanorod assembly from solution: influence of concentration, charge and solvent nature , 2012 .

[35]  T. Moritz,et al.  Ice-mould freeze casting of porous ceramic components , 2007 .

[36]  A. Nakajima,et al.  Preparation and properties of porous alumina ceramics with uni-directionally oriented pores by extrusion method using a plastic substance as a pore former , 2007 .

[37]  N. M. Gokhale,et al.  Preparation of macroporous alumina ceramics using wheat particles as gelling and pore forming agent , 2007 .

[38]  S. Corbin,et al.  Influence of green formulation and pyrolyzable particulates on the porous microstructure and sintering characteristics of tape cast ceramics , 2001 .

[39]  S. Kanzaki,et al.  Synthesis of Porous Ceramics with Complex Pore Structure by Freeze‐Dry Processing , 2001 .

[40]  K. Uematsu,et al.  Influence of temperature on stability of aqueous alumina slurry containing polyelectrolyte dispersant , 1997 .

[41]  P. Sepulveda.  Gelcasting foams for porous ceramics , 1997 .

[42]  D. S. Pearson,et al.  Viscosity and Yield Stress of Alumina Slurries Containing Large Concentrations of Electrolyte , 1994 .

[43]  L. Gauckler,et al.  Shaping of ceramic green compacts direct from suspensions by enzyme catalyzed reactions , 1994 .