Heat insulation performance, mechanics and hydrophobic modification of cellulose-SiO2 composite aerogels.

Cellulose-SiO2 composite hydrogel was prepared by combining the NaOH/thiourea/H2O solvent system and the immersion method with controlling the hydrolysis-fasculation rate of tetraethyl orthosilicate (TEOS). The hydrophobic composite aerogels were obtained through the freeze-drying technology and the cold plasma modification technology. Composite SiO2 could obviously reduce the thermal conductivity of cellulose aerogel. The thermal conductivity could be as low as 0.026 W/(mK). The thermal insulation mechanism of the aerogel material was discussed. Composite SiO2 reduced hydrophilicity of cellulose aerogel, but environmental humidity had a significant influence on heat insulation performance. After hydrophobic modification using CCl4 as plasma was conducted, the surface of composite aerogel was changed from hydrophilic to hydrophobic and water contact angle was as high as 132°. The modified composite aerogel still kept good heat insulation performance. This work provided a foundation for the possibility of applying cellulose-SiO2 composite aerogel in the insulating material field.

[1]  H. Sugimura,et al.  Wettablity of Poly(ethylene terephthalate) Substrates Modified by a Two‐Step Plasma Process: Ultra Water Repellent Surface Fabrication , 2004 .

[2]  D. Teeters,et al.  Processing of low-density silica gel by critical point drying or ambient pressure drying , 2001 .

[3]  Mohammad Hasan Abbasi,et al.  Silica aerogel; synthesis, properties and characterization , 2008 .

[4]  Pierre-Olivier Chapuis,et al.  Nanoscale heat transfer at contact between a hot tip and a substrate , 2006 .

[5]  Jianjun Shi,et al.  Reinforced low density alginate-based aerogels: Preparation, hydrophobic modification and characterization , 2012 .

[6]  M. Wendland,et al.  Cellulosic aerogels as ultra-lightweight materials. Part 2: Synthesis and properties 2nd ICC 2007, Tokyo, Japan, October 25–29, 2007 , 2008 .

[7]  S. Kelley,et al.  Synthesis and characterization of dense and porous cellulose films , 2007 .

[8]  S. Kistler,et al.  Coherent Expanded Aerogels and Jellies. , 1931, Nature.

[9]  J. Innerlohinger,et al.  Aerocellulose: Aerogels and Aerogel‐like Materials made from Cellulose , 2006 .

[10]  D. Evtuguin,et al.  Synthesis and characterisation of cellulose/silica hybrids obtained by heteropoly acid catalysed sol-gel process , 2007 .

[11]  Alexander A. Balandin,et al.  Phonon heat conduction in a semiconductor nanowire , 2001 .

[12]  A. Hunt,et al.  Mean Free Path and Apparent Thermal Conductivity of a Gas in a Porous Medium , 1995 .

[13]  J. Feijen,et al.  Immobilization of functionalized alkyl-poly(ethylene oxide) surfactants on poly(ethylene) surfaces by means of an argon plasma treatment. , 1997, Journal of biomaterials science. Polymer edition.

[14]  Fabienne Poncin-Epaillard,et al.  Synthesis of transparent superhydrophobic polyethylene surfaces , 2006 .

[15]  Wei Huang,et al.  Surface modification of polyimide films via plasma polymerization and deposition of allylpentafluorobenzene , 2002 .

[16]  J. Badyal,et al.  Pulsed Plasma Deposition of Super-Hydrophobic Nanospheres , 2002 .

[17]  R. L. Earle.  CHAPTER 5 – HEAT-TRANSFER THEORY , 1983 .

[18]  T. Budtova,et al.  Aerocellulose: new highly porous cellulose prepared from cellulose-NaOH aqueous solutions. , 2008, Biomacromolecules.

[19]  R. A. Young,et al.  Surface fluorination of paper in CF4-RF plasma environments , 2002 .

[20]  L. Ratke,et al.  Synthesis and characterisation of nanofibrillar cellulose aerogels , 2008 .

[21]  Gang Chen,et al.  Phonon heat conduction in nanostructures , 2000 .

[22]  T. Chandy,et al.  Use of plasma glow for surface-engineering biomolecules to enhance bloodcompatibility of Dacron and PTFE vascular prosthesis. , 2000, Biomaterials.

[23]  M. Bousmina,et al.  Biodegradable polymers and their layered silicate nanocomposites: In greening the 21st century materials world , 2005 .

[24]  W. Brown,et al.  A viscosity-molecular weight relationship for cellulose in cadoxen and a hydrodynamic interpretation , 1965 .

[25]  Lina Zhang,et al.  Cellulose aerogels from aqueous alkali hydroxide-urea solution. , 2008, ChemSusChem.

[26]  S. Henning,et al.  Production of Silica Aerogel , 1981 .

[27]  Zhang Yanhua,et al.  Preparation of Nano-Silver Flake by Chemical Reduction Method , 2010 .

[28]  S. Kistler.  Coherent Expanded-Aerogels , 1931 .

[29]  Se-Young Choi,et al.  Ambient-dried silica aerogel doped with TiO2 powder for thermal insulation , 2000 .

[30]  P. Achard,et al.  Cellulose-based aerogels , 2006 .

[31]  F. Schwertfeger,et al.  Applications for silica aerogel products , 1998 .

[32]  Lina Zhang,et al.  Microporous membranes prepared from cellulose in NaOH/thiourea aqueous solution , 2004 .

[33]  M. Phisalaphong,et al.  Novel nanoporous membranes from regenerated bacterial cellulose , 2008 .