Structural modifications of the thick polysilicon layers on silicon during phosphorus diffusion: contributing mechanisms

TEM investigations of the LP-LT-CVD thick (1500 nm) polySi layer on 16 nm SiO/sub 2//Si allow one to introduce specific mechanisms to explain the fast polySi regrowth and the SiO/sub 2/ degradation during a short-time (15 min.) moderate (1030/spl deg/C) heat-temperature treatment and during a subsequent 20 min., 1030/spl deg/C annealing.

J. Stoemenos | C. Postolache | F. Gaisenu | C. A. Drimitriadis | C. Angelis

[1] Dieter G. Ast,et al. Effects of the presence/absence of HCl during gate oxidation on the electrical and structural properties of polycrystalline silicon thin‐film transistors , 1989 .

[2] H. Schaber,et al. Analysis of Polysilicon Diffusion Sources , 1988 .

[3] W. Schröter,et al. Contribution of Diffusion Interstitial Injection to Gettering of Metallic Impurities in Silicon , 1996 .

[4] C. Tsamis,et al. Suppression mechanisms for oxidation stacking faults in silicon on insulator , 1992 .