Nanostructured black silicon and the optical reflectance of graded-density surfaces

We fabricate and measure graded-index “black silicon” surfaces and find the underlying scaling law governing reflectance. Wet etching (100) silicon in HAuCl4, HF, and H2O2 produces Au nanoparticles that catalyze formation of a network of [100]-oriented nanopores. This network grades the near-surface optical constants and reduces reflectance to below 2% at wavelengths from 300 to 1000 nm. As the density-grade depth increases, reflectance decreases exponentially with a characteristic grade depth of about 1/8 the vacuum wavelength or half the wavelength in Si. Observation of Au nanoparticles at the ends of cylindrical nanopores confirms local catalytic action of moving Au nanoparticles.

[1]  Claude de Bellefon,et al.  Enhancing surface activity in silicon microreactors: Use of black silicon and alumina as catalyst supports for chemical and biological applications , 2008 .

[2]  M. Hutley,et al.  The Optical Properties of 'Moth Eye' Antireflection Surfaces , 1982 .

[3]  Ernst-Bernhard Kley,et al.  Terahertz emission from black silicon , 2008 .

[4]  R. L. Williamson,et al.  Optical properties of gold colloids formed in inverse micelles , 1993 .

[5]  Martin Stutzmann,et al.  Black nonreflecting silicon surfaces for solar cells , 2006 .

[6]  Michio Matsumura,et al.  Texturization of multicrystalline silicon wafers for solar cells by chemical treatment using metallic catalyst , 2006 .

[7]  Jun Shao,et al.  Wide-band “black silicon” based on porous silicon , 2006 .

[8]  T. Chow,et al.  Reactive Ion Etching of Silicon in CCl4 and HCl Plasmas , 1987 .

[9]  Eric Mazur,et al.  Near-unity below-band-gap absorption by microstructured silicon , 2001 .

[10]  Michael Fischer,et al.  Bonding of silicon with filled and unfilled polymers based on black silicon , 2007 .

[11]  G. Cody,et al.  Optical reflectance and transmission of a textured surface , 1977 .

[12]  K. Nishioka,et al.  Antireflection subwavelength structure of silicon surface formed by wet process using catalysis of single nano-sized gold particle , 2008 .

[13]  D. Gräf,et al.  Influence of HF‐H2O2 treatment on Si(100) and Si(111) surfaces , 1993 .

[14]  K. Tsujino,et al.  Boring Deep Cylindrical Nanoholes in Silicon Using Silver Nanoparticles as a Catalyst , 2005 .

[15]  Xiuling Li,et al.  Metal-assisted chemical etching in HF/H2O2 produces porous silicon , 2000 .