The effect of solvent on the etching of ITO electrode

Abstract In this study, the effect of solvents, HCl and aqua regia at room temperature, on the etching behavior of ITO film was investigated. A higher etching rate was obtained in aqua regia than in HCl. However, via XPS analysis, it was found that there was more surface residual byproduct in aqua regia etchant than in HCl. The surface concentration (ratio of chlorine to indium) was 7.2 and 0.38 in aqua regia and HCl, respectively. It was also observed that the surface residual byproduct reduced the carrier mobility due to the ionized impurity scattering. As seen in the ITO pattern after the etching process, a serious undercut occurred with the aqua regia due to the fast etching rate. Thus, the 9 M HCl solution is more suitable as an etchant for ITO/OLED application.

[1]  Xiaoyuan Hou,et al.  Bubble formation in organic light-emitting diodes , 2000 .

[2]  D. Briggs,et al.  Practical surface analysis: By auger and x-ray photoelectron spectroscopy , 1983 .

[3]  J. E. Meerakker,et al.  On the Mechanism of ITO Etching: The Specificity of Halogen Acids , 1993 .

[4]  T. Matsuoka,et al.  Patterning Characteristics of ITO Thin Films , 1989 .

[5]  Louis M. Leung,et al.  Surface preparation and characterization of indium tin oxide substrates for organic electroluminescent devices , 1999 .

[6]  T. J. Vink,et al.  On the homogeneity of sputter-deposited ITO films Part II. Etching behaviour , 1995 .

[7]  D. Paine,et al.  Study of the effect of Sn doping on the electronic transport properties of thin film indium oxide , 1993 .

[8]  S. M. Sze,et al.  Physics of semiconductor devices , 1969 .

[9]  S. Forrest,et al.  Reliability and degradation of organic light emitting devices , 1994 .

[10]  G. Frank,et al.  Electrical properties and defect model of tin-doped indium oxide layers , 1982 .

[11]  Shui-Tong Lee,et al.  Modification of the hole injection barrier in organic light-emitting devices studied by ultraviolet photoelectron spectroscopy , 2000 .

[12]  D. Milliron,et al.  Surface oxidation activates indium tin oxide for hole injection , 2000 .

[13]  N. Koch,et al.  Combined XPS, AFM, TEM and ellipsometric studies on nanoscale layers in organic light emitting diodes , 2002 .

[14]  C. M. Melliar‐Smith,et al.  V-2 – Plasma-Assisted Etching Techniques for Pattern Delineation , 1978 .

[15]  A. J. Hughes,et al.  Etching methods for indium oxide/tin oxide films , 1976 .

[16]  Shui-Tong Lee,et al.  Metal diffusion from electrodes in organic light-emitting diodes , 1999 .