Metallic coating of aerospace carbon/epoxy composites by the pulsed gas dynamic spraying process

A method for applying metallic coatings to high fibre volume fraction aerospace carbon/epoxy polymer matrix composites is presented. The pulsed gas dynamic spraying process was used for depositing zinc coatings on composites featuring a thin layer of copper particles co-cured into the laminate. No surface preparation was required on the cured substrates prior to spraying hence no damage was induced in brittle carbon fibres. Polymer matrix composite substrates with an added layer of co-cured copper particles were manufactured using a standard autoclave process. External substrate heating was not required. Metal powder and epoxy degradation were avoided through low process temperatures. Satisfactory cohesive and adhesive characteristics, low porosities and good microhardness values were obtained for a range of coating parameters. Microhardness and porosity of coatings deposited on polymer matrix composites compared well with those of similar coatings deposited on metallic substrates.

[1]  James H. Starnes,et al.  Design and manufacturing of aerospace composite structures, state-of-the-art assessment , 2002 .

[2]  A. Liu,et al.  Influence of bond coat on shear adhesion strength of erosion and thermal resistant coating for carbon fiber reinforced thermosetting polyimide , 2006 .

[3]  K. Taylor,et al.  Sputtering on polymeric composites , 1990 .

[4]  G. Palmese,et al.  Adhesive/cohesive properties of thermally sprayed functionally graded coatings for polymer matrix composites , 2005 .

[5]  Hamid Assadi,et al.  Bonding mechanism in cold gas spraying , 2003 .

[6]  S. M. Vyawahare.  Protective thermal spray coatings for polymer matrix composites , 2006 .

[7]  Surya R. Kalidindi,et al.  Solid particle erosion resistance of thermally sprayed functionally graded coatings for polymer matrix composites , 2006 .

[8]  U. V. Diccar.  Plasma spray coatings for polymer composites , 2006 .

[9]  S. K. Naik,et al.  Erosion Coatings for Polymer Matrix Composites in Propulsion Applications , 2003 .

[10]  B. Jodoin,et al.  Cermet coatings prepared by pulsed gas dynamic spraying process : Effect of the process parameters , 2008 .

[11]  T. Vansteenkiste,et al.  Fracture study of aluminum composite coatings produced by the kinetic spray method , 2005 .

[12]  J. Schoenung,et al.  Synthesis and mechanical properties of nanocrystalline Ni coatings produced by cold gas dynamic spraying , 2006 .

[13]  L. Ajdelsztajn,et al.  Pulsed-Gas Dynamic Spraying: Process analysis, development and selected coating examples , 2007 .

[14]  Aiguo Liu,et al.  Arc sprayed erosion-resistant coating for carbon fiber reinforced polymer matrix composite substrates , 2006 .

[15]  G. Palmese,et al.  Erosion/Oxidation Resistant Coatings for High Temperature Polymer Composites , 2003 .

[16]  J. Schoenung,et al.  Cold spray deposition of nanocrystalline aluminum alloys , 2005 .

[17]  D. Hirschfeld,et al.  Effect of Surface Modification on Adhesion of a Metal Bond Coat to PMR Composites , 2005 .

[18]  B. Jodoin.  Cold spray nozzle mach number limitation , 2002 .

[19]  E. Sansoucy,et al.  WC-based cermet coatings produced by cold gas dynamic and pulsed gas dynamic spraying processes , 2007 .