Platinum catalysed wet oxidation of phenol in a stirred slurry reactor: A practical operation window

Abstract The catalytic performance of graphite supported platinum (5 wt.%) catalyst in liquid phase oxidation has been studied using a continuous flow stirred tank slurry reactor (CSTR) in order to determine the proper operation window. The study was carried out in a temperature range of 120–180 °C and in a total pressure range of 1.5–2.0 MPa. Other operational variables employed were oxygen partial pressure (0.01–0.8 MPa), initial phenol feed concentration (0.005–0.07 M), and catalyst concentration from 1 to 10 kg m −3 . It was found that the extent of oxygen coverage on the platinum surface determines the reaction pathway and selectivity to CO 2 and H 2 O. Complete oxidation of phenol to CO 2 and H 2 O could be achieved at 150 °C when the reaction proceeds within the range of weight specific oxygen loads of 0.15–0.35 mol s −1  kg Pt −1 and at stoichiometric oxygen excess in the range of 0–80%. The activity of the platinum catalyst remained high when the residual partial pressure of oxygen in the reactor was kept below 150 kPa. Higher residual oxygen partial pressure resulted into deactivation of the platinum catalyst (over-oxidation), which was temporary and could be reversed at reducing conditions. The formation of p -benzoquinone, followed by the formation of polymeric products was also favoured at higher oxygen load, which resulted into permanent deactivation of the platinum catalyst (poisoning). While the platinum surface was vulnerable to poisoning by carbonaceous compounds when insufficient oxygen was used, a fully reduced platinum surface favoured the formation of acetic and succinic acids which are difficult to oxidize. Higher temperatures can enhance the activity of the platinum catalyst, while at lower temperatures catalyst deactivation occurs with increased formation of polymeric products and lower selectivity to CO 2 and H 2 O. In order to maintain the catalyst within the proper operation window, a CSTR is the preferred reactor.

[1]  J. Barbier,et al.  Catalytic oxidation of maleic and oxalic acids under potential control of platinum catalysts , 1999 .

[2]  Effect of chemical oxidation on anaerobic biodegradation of model phenolic compounds , 1992 .

[3]  Stefano Peratello,et al.  Experimental methods in catalytic kinetics , 1999 .

[4]  Don W. Green,et al.  Perry's chemical engineers' handbook. 7th ed. , 1997 .

[5]  Y. Sano,et al.  MASS TRANSFER COEFFICIENTS FOR SUSPENDED PARTICLES IN AGITATED VESSELS AND BUBBLE COLUMNS , 1974 .

[6]  Van Santen,et al.  Low temperature oxidation of ammonia to nitrogen in liquid phase , 1999 .

[7]  P. Gallezot,et al.  Selective oxidation of alcohols and aldehydes on metal catalysts , 2000 .

[8]  A. Baiker,et al.  Oxidation of alcohols with molecular oxygen on platinum metal catalysts in aqueous solutions , 1994 .

[9]  J. Levec,et al.  Catalytic oxidation of aqueous solutions of organics. An effective method for removal of toxic pollutants from waste waters , 1995 .

[10]  A. Akgerman,et al.  Catalytic wet oxidation of phenol over a Pt/TiO catalyst , 1997 .

[11]  J. Figueiredo,et al.  Catalytic wet air oxidation of low molecular weight carboxylic acids using a carbon supported platinum catalyst , 2000 .

[12]  G. Marin,et al.  Selective oxidation of methyl alpha-D-glucopyranoside with oxygen over supported platinum : kinetic modeling in the presence of deactivation by overoxidation of the catalyst , 1997 .

[13]  Jyeshtharaj B. Joshi,et al.  Wet air oxidation , 1995 .

[14]  J. Foussard,et al.  Treatment of organic aqueous wastes: Wet air oxidation and Wet Peroxide Oxidation. , 1996, Environmental pollution.

[15]  M. Sheintuch,et al.  Catalytic Abatement of Water Pollutants , 1998 .

[16]  F. Luck,et al.  Wet air oxidation: past, present and future , 1999 .

[17]  B. Kuster,et al.  Catalyst deactivation and reactivation during aqueous alcohol oxidation in a redox-cycle reactor , 1999 .

[18]  J. Carberry,et al.  Biodegradation of PCP enhanced by chemical oxidation pretreatment , 1992 .

[19]  G. Marin,et al.  Kinetic modeling for wet air oxidation of formic acid on a carbon supported platinum catalyst , 1997 .

[20]  W.P.M. van Swaaij,et al.  Mass transfer in gas-liquid slurry reactors , 1993 .

[21]  B. Kuster,et al.  Platinum catalysed aqueous alcohol oxidation: experimental studies and reaction model discrimination , 2000 .

[22]  Phillip E. Savage,et al.  Organic Chemical Reactions in Supercritical Water. , 1999, Chemical reviews.

[23]  F. García-Ochoa,et al.  Oxidation of phenol in aqueous solution with copper catalysts , 2001 .

[24]  G. Marin,et al.  Engineering aspects of the aqueous noble metal catalysed alcohol oxidation , 2000 .

[25]  Aydin Akgerman,et al.  Advanced oxidation of phenolic compounds , 2000 .