Synergistic flame retardant effect of poly(ether sulfones) and polysiloxane on polycarbonate

Flame retardance of bisphenol A polycarbonate (PC) was improved by the co-addition of poly (ether sulfones) (PES) and polysiloxane/acrylate copolymer (PSiA) while retaining a high rigidity and toughness. A UL 94 V-0 rating for 1.6-mm thick samples of PC/PES/PSiA blend with 10.0 wt % PES and 0.5 wt % PSiA (PC/10PES/0.5PSiA) was obtained. Its average heat release rate (av-HRR) in a cone calorimeter measurement was decreased by 19% on the basis of PC/PES blend with 10.0 wt % PES. Scanning electron microscopy (SEM) morphologies of impact-fractured surfaces revealed that the incorporation of 0.5 wt % PSiA decreased the dimensions of PES dispersed phase and provoked the uniform distribution of PES in PC matrix. Thermogravimetric-Fourier transform infrared spectroscopy analysis results revealed that PSiA dominantly promoted the degradation of PC and the degraded products were combined with PES to form a superior flame-retarded carbon layer. A higher sulfur and silicon content on the residue surface after vertical burning tests detected by SEM/energy dispersive spectrometer signified their accumulation during combustion. © 2011 Wiley Periodicals, Inc. J Appl Polym Sci, 2011

[1]  Ying‐Ling Liu,et al.  The effect of silicon sources on the mechanism of phosphorus-silicon synergism of flame retardation of epoxy resins , 2005 .

[2]  B. Schartel,et al.  The effect of different impact modifiers in halogen-free flame retarded polycarbonate blends - II. Fire behaviour , 2009 .

[3]  Ying‐Ling Liu,et al.  Phosphorus‐containing epoxy resins for flame retardancy V: Synergistic effect of phosphorus–silicon on flame retardancy , 2000 .

[4]  L. An,et al.  Note: Interfacial layer and phase inversion behavior in the blend of polyethersulfone and polycarbonate , 1998 .

[5]  Xin Bai,et al.  Thermal degradation behavior of low‐halogen flame retardant PC/PPFBS/PDMS , 2011 .

[6]  A. Ballistreri,et al.  Intumescent flame retardants for polymers. IV. The polycarbonate–aromatic sulfonates system , 1988 .

[7]  Jianqing Zhao,et al.  Preparation and characterization of copolymerized aminopropyl/phenylsilsesquioxane microparticles , 2005 .

[8]  T. Kanai,et al.  Thermal decomposition behavior and flame retardancy of polycarbonate containing organic metal salts: Effect of salt composition , 2004 .

[9]  V. Zaporojtchenko,et al.  Functional Polymer Nanocomposites , 2008 .

[10]  S. Levchik,et al.  Overview of recent developments in the flame retardancy of polycarbonates , 2005 .

[11]  Zhenhua Jiang,et al.  Effect of Random Copolymers of 2,2‐Di(4‐hydroxy Phenyl) and 4,4′‐Dihydroxyldiphenylsulfone on the Morphology and Mechanical Properties of Polyethersulfone and Polycarbonate Blends , 2007 .

[12]  C. Morterra,et al.  Infrared studies of carbons. XII The formation of chars from a polycarbonate , 1990 .

[13]  R. Weiss,et al.  The effect of tosylate salts and zinc sulfonated polystyrene ionomer on the thermal stability of bisphenol A polycarbonate , 2004 .

[14]  S. Serizawa,et al.  Silicone derivatives as new flame retardants for aromatic thermoplastics used in electronic devices , 1998 .

[15]  Yu-Zhong Wang,et al.  Thermal behaviors of flame‐retardant polycarbonates containing diphenyl sulfonate and poly(sulfonyl phenylene phosphonate) , 2003 .

[16]  L. Perng.  Thermal degradation mechanism of poly(arylene sulfone)s by stepwise Py‐GC/MS , 2000 .

[17]  Ying‐Ling Liu,et al.  Preparation and properties of high performance epoxy–silsesquioxane hybrid resins prepared using a maleimide–alkoxysilane compound as a modifier , 2005 .

[18]  Claire Longuet,et al.  Flame retardancy of silicone-based materials , 2009 .

[19]  L. Perng.  Comparison of thermal degradation characteristics of poly(arylene sulfone)s using thermogravimetric analysis/mass spectrometry , 2001 .