Lightning strike damage detection at a fastener using self-sensing TDR of composite plate

Abstract Carbon fibre reinforced polymer (CFRP) composites structures are widely used in aeroplane structures. When a lightning strike affects fasteners or leak electric current of the lightning strike arrives at fasteners, the fasteners play serve as conducting electrodes for the CFRP plate. This current might cause complicated damage in the CFRP plate. The authors have developed self-sensing TDR to detect damage. Self-sensing TDR is used in this study to monitor lightning strike damage around a CFRP plate fastener hole. The lightning strike electric current is applied directly to a fastener. Thereafter, self-sensing TDR is applied. The lightning strike damage is investigated using cross-sectional inspection to clarify the mechanisms of the monitoring using TDR. Results show that the method can detect a 30 kA strike. Peeling of the GFRP insulator causes a characteristic impedance change, which in turn causes signal reflection of the transmission line.

[1]  S. Al-Hassani,et al.  ELECTRICAL RESISTANCE MEASUREMENT TECHNIQUE FOR DETECTING FAILURE IN CFRP MATERIALS AT HIGH STRAIN RATES , 1994 .

[2]  Dae-Cheol Seo,et al.  Damage detection of CFRP laminates using electrical resistance measurement and neural network , 1999 .

[3]  Phil E. Irving,et al.  Fatigue damage characterization in carbon fibre composite materials using an electrical potential technique , 1998 .

[4]  Yoshiro Suzuki,et al.  Impact damage detection of a carbon-fibre-reinforced-polymer plate employing self-sensing time-domain reflectometry , 2015 .

[5]  Akira Todoroki,et al.  Self-Sensing TDR for Bearing Failure Detection of CFRP Laminate Fastener Hole with Particular Reference to the Effect of Fasteners , 2015 .

[6]  Yoshiyasu Hirano,et al.  Coupled thermal–electrical analysis for carbon fiber/epoxy composites exposed to simulated lightning current , 2010 .

[7]  Akira Todoroki,et al.  Artificial lightning testing on graphite/epoxy composite laminate , 2010 .

[8]  Mark A. Miller,et al.  Damage resistance and tolerance of carbon/epoxy composite coupons subjected to simulated lightning strike , 2009 .

[9]  A. Chateauminois,et al.  In situ detection of damage in CFRP laminates by electrical resistance measurements , 1999 .

[10]  Gilles Lubineau,et al.  Electrical behavior of laminated composites with intralaminar degradation: A comprehensive micro-meso homogenization procedure , 2014 .

[11]  David Pommerenke,et al.  Crack detection of a full-scale reinforced concrete girder with a distributed cable sensor , 2005 .

[12]  Akira Todoroki,et al.  Self-sensing time domain reflectometry method for damage monitoring of a CFRP plate using a narrow-strip transmission line , 2014 .

[13]  Akira Todoroki,et al.  Delamination identification of cross-ply graphite/epoxy composite beams using electric resistance change method , 2002 .

[14]  Akira Todoroki,et al.  Measurement of orthotropic electric conductance of CFRP laminates and analysis of the effect on delamination monitoring with an electric resistance change method , 2002 .

[15]  Akira Todoroki,et al.  Damage Monitoring of CFRP Plate Using Self-Sensing TDR Method , 2012 .

[16]  D. Chung,et al.  Carbon fiber reinforced concrete for smart structures capable of non-destructive flaw detection , 1993 .

[17]  Akira Todoroki,et al.  Self-Sensing Curved Micro-Strip Line Method for Damage Detection of CFRP Composites , 2014 .

[18]  M. K. Yoon,et al.  A Time-domain Reflectometry Method for Automated Measurement of Crack Propagation in Composites during Mode I DCB Testing , 2006 .

[19]  Akira Todoroki,et al.  Numerical Simulation of Self-Sensing Time Domain Reflectometry for Damage Detection of Carbon Fiber Reinforced Polymer Plate , 2012 .

[20]  Karl Schulte,et al.  Load and failure analyses of CFRP laminates by means of electrical resistivity measurements , 1989 .

[21]  Ayo O. Abatan,et al.  Development of an electrical time domain reflectometry (ETDR) distributed strain sensor , 2005 .

[22]  H. A. Wheeler Transmission-Line Properties of a Strip Line Between Parallel Planes , 1978 .

[23]  Keiji Ogi,et al.  Characterization of piezoresistance behavior in a CFRP unidirectional laminate , 2005 .

[24]  Hiroaki Yanagida,et al.  Preventing Fatal Fractures in Carbon‐Fiber–Glass‐Fiber‐Reinforced Plastic Composites by Monitoring Change in Electrical Resistance , 1993 .