The state of Pb-free solder — A joint reliability overview

Over the past decade the electronics components industry successfully transitioned from the use of leaded solder to lead-free (Pb-free) solders in response to growing environmental health concerns related to heavy metals and other substances. Pbfree components in general are in compliance to meet the European restriction of hazardous substances (RoHS) directives. During the transition period to Pb-free surface mount, numerous issues were raised about the selected alloys, the board assembly process and reliability. Early Pb-free reliability concerns were due to incomplete analytical understanding of the Tin-Silver-Copper solder creep-fatigue behavior, difficulty in computing the magnitude of ball grid array (BGA) relative displacements or strains and lack of product field history. Since then the failure mechanisms were characterized and many models are in common use for reliability estimation and design. This manuscript revisits the initial concerns, reliability model use evolution and summarizes the current understanding that has resulted in a decade of reliable field operation for the Pb-free SAC solders selected.

[1]  Xuejun Fan,et al.  Slow Cycle Fatigue Creep Performance of Pb-Free (LF) Solders , 2007, 2007 Proceedings 57th Electronic Components and Technology Conference.

[2]  C. Handwerker,et al.  Experimental and thermodynamic assessment of Sn-Ag-Cu solder alloys , 2000 .

[4]  Klas Andersson,et al.  Re-calibration of Engelmaier's Model for Leadless, Lead-free Solder Attachments , 2007, Qual. Reliab. Eng. Int..

[5]  Keith C. Norris,et al.  Reliability of controlled collapse interconnections , 1969 .

[6]  Ronglu Sun.  APPLICABILITY OF VARIOUS Pb-FREE SOLDER JOINT ACCELERATION FACTOR MODELS , 2006 .

[7]  M. Osterman,et al.  Life expectancies of Pb-free SAC solder interconnects in electronic hardware , 2006 .

[8]  O. Salmela,et al.  Acceleration Factors for Lead-Free Solder Materials , 2007, IEEE Transactions on Components and Packaging Technologies.

[9]  Frankel's theorem in the symplectic category , 2002, math/0204016.

[10]  Mudasir Ahmad,et al.  Parametric acceleration transforms for lead-free solder joint reliability under thermal cycling conditions , 2009, 2009 59th Electronic Components and Technology Conference.

[11]  Xuejun Fan,et al.  Effects of Dwell Time and Ramp Rate on Lead-Free Solder Joints in FCBGA Packages , 2005, Proceedings Electronic Components and Technology, 2005. ECTC '05..

[12]  Xuejun Fan,et al.  An acceleration model for lead-free (SAC) solder joint reliability under thermal cycling , 2008, 2008 58th Electronic Components and Technology Conference.

[13]  P. Lall,et al.  Thermal cycling reliability of lead free solders for automotive applications , 2004, The Ninth Intersociety Conference on Thermal and Thermomechanical Phenomena In Electronic Systems (IEEE Cat. No.04CH37543).

[14]  J. Clech.  Lead-Free and Mixed Assembly Solder Joint Reliability Trends , 2004 .

[15]  Min Pei,et al.  A preliminary solder joint life prediction model by experiment and simulation for translation of use condition to temperature cycling test condition , 2013, 2013 IEEE 63rd Electronic Components and Technology Conference.

[16]  A. Syed.  Accumulated creep strain and energy density based thermal fatigue life prediction models for SnAgCu solder joints , 2004, 2004 Proceedings. 54th Electronic Components and Technology Conference (IEEE Cat. No.04CH37546).

[17]  Robert Darveaux,et al.  Solder Joint Fatigue Life Model , 1997 .

[18]  Michael Pecht,et al.  Solder Creep-Fatigue Analysis by an Energy-Partitioning Approach , 1992 .