Tribological behavior of Ti6Al4V cellular structures produced by Selective Laser Melting.

Additive manufacturing (AM) technologies enable the fabrication of innovative structures with complex geometries not easily manufactured by traditional processes. Regarding metallic cellular structures with tailored/customized mechanical and wear performance aiming to biomedical applications, Selective Laser Melting (SLM) is a remarkable solution for their production. Focusing on prosthesis and implants, in addition to a suitable Young's modulus it is important to assess the friction response and wear resistance of these cellular structures in a natural environment. In this sense, five cellular Ti6Al4V structures with different open-cell sizes (100-500µm) were designed and produced by SLM. These structures were tribologicaly tested against alumina using a reciprocating sliding ball-on-plate tribometer. Samples were submerged in Phosphate Buffered Saline (PBS) fluid at 37°C, in order to mimic in some extent the human body environment. The results showed that friction and wear performance of Ti6Al4V cellular structures is influenced by the structure open-cell size. The higher wear resistance was obtained for structures with 100µm designed open-cell size due to the higher apparent area of contact to support tribological loading.

[1]  Alain Iost,et al.  Tribological behavior of Ti-6Al-4V and Ti-6Al-7Nb Alloys for Total Hip Prosthesis , 2014 .

[2]  K. Anselme,et al.  Osteoblast adhesion on biomaterials. , 2000, Biomaterials.

[3]  Liang Hao,et al.  Advanced lightweight 316L stainless steel cellular lattice structures fabricated via selective laser melting , 2014 .

[4]  L Cristofolini,et al.  Large-sliding contact elements accurately predict levels of bone-implant micromotion relevant to osseointegration. , 2000, Journal of biomechanics.

[5]  A. Bandyopadhyay,et al.  Influence of porosity on mechanical properties and in vivo response of Ti6Al4V implants. , 2010, Acta biomaterialia.

[6]  S. Chauhan,et al.  Dry Sliding Wear Behaviour of Titanium (Grade 5) Alloy by Using Response Surface Methodology , 2013 .

[7]  N. Alves,et al.  Predictive models for physical and mechanical properties of Ti6Al4V produced by Selective Laser Melting , 2016 .

[8]  Konda Gokuldoss Prashanth,et al.  Mechanical Behavior of Porous Commercially Pure Ti And Ti–TiB Composite Materials Manufactured By Selective Laser Melting , 2015 .

[9]  Rainer Bader,et al.  Influence of the structural orientation on the mechanical properties of selective laser melted Ti6Al4V open-porous scaffolds , 2016 .

[10]  Iduvirges Lourdes Muller,et al.  Tribological, electrochemical and tribo-electrochemical characterization of bare and nitrided Ti6Al4V in simulated body fluid solution. , 2011 .

[11]  Artur Mateus,et al.  Predictive models for physical and mechanical properties of 316L stainless steel produced by selective laser melting , 2016 .

[12]  H. Rack,et al.  Friction and surface behavior of selected titanium alloys during reciprocating-sliding motion , 2001 .

[13]  Jan Wieding,et al.  Numerical optimization of open-porous bone scaffold structures to match the elastic properties of human cortical bone. , 2014, Journal of the mechanical behavior of biomedical materials.

[14]  Tomiharu Matsushita,et al.  Effect of pore size on bone ingrowth into porous titanium implants fabricated by additive manufacturing: An in vivo experiment. , 2016, Materials science & engineering. C, Materials for biological applications.

[15]  Liang Hao,et al.  Ti-6Al-4V triply periodic minimal surface structures for bone implants fabricated via selective laser melting. , 2015, Journal of the mechanical behavior of biomedical materials.

[16]  Changsheng Liu,et al.  Biomimetic porous scaffolds for bone tissue engineering , 2014 .

[17]  B. Henriques,et al.  Comparison between PEEK and Ti6Al4V concerning micro-scale abrasion wear on dental applications. , 2016, Journal of the mechanical behavior of biomedical materials.

[18]  R. M. Filho,et al.  Functionalization of Ti6Al4V scaffolds produced by direct metal laser for biomedical applications , 2015 .

[19]  Abhay Pandit,et al.  Fabrication methods of porous metals for use in orthopaedic applications. , 2006, Biomaterials.

[20]  Bikramjit Basu,et al.  Low temperature additive manufacturing of three dimensional scaffolds for bone-tissue engineering applications: Processing related challenges and property assessment , 2016 .

[21]  R. Emadi,et al.  Fabrication and characterization of nanostructure diopside scaffolds using the space holder method: Effect of different space holders and compaction pressures , 2016 .

[22]  Damiano Pasini,et al.  Compensation strategy to reduce geometry and mechanics mismatches in porous biomaterials built with Selective Laser Melting. , 2017, Journal of the mechanical behavior of biomedical materials.