Comparison of glass etching properties between HCl and HNO3 solution

A comparison of glass etching properties between HCl and HNO3 solution is presented in this paper, which allows us to predict the etched product's shape under a variety of etching conditions, mask compensation and multiple processing steps. Four conclusions could be draw from the experiments. First, the best concentration ratio of the etching solution to protect the mask from damage and get a channel with depth of 40 μm is HF:HCl:NH4F=5.5mol/L:4mol/L:2.5mol/L. Second, as the temperature increases, the longitudinal etching rate increases. However, the temperature has little influence on the lateral erosion ratio when the temperature gets high. Third, HCl has a better surface morphology against HNO3 as an addition to solution. Last, the mask will introduce strain because of sputtering, which is harmful to the glass etching..

[1]  A. Evans,et al.  A new masking technology for deep glass etching and its microfluidic application , 2004 .

[2]  Jianmin Miao,et al.  Deep wet etching-through 1mm pyrex glass wafer for microfluidic applications , 2007, 2007 IEEE 20th International Conference on Micro Electro Mechanical Systems (MEMS).

[3]  M.-A. Grétillat,et al.  A New Fabrication Method for Borosilicate Glass Capillary Tubes with Lateral Inlets and Outlets , 1997 .

[4]  Ciprian Iliescu,et al.  Deep Wet and Dry Etching of Pyrex Glass : a Review , 2005 .

[5]  A. Offenhäusser,et al.  The evaporated metal masks for chemical glass etching for BioMEMS , 2005 .

[6]  G. Stemme,et al.  Deep wet etching of borosilicate glass using an anodically bonded silicon substrate as mask , 1998 .

[7]  Ciprian Iliescu,et al.  Defect-free wet etching through pyrex glass using Cr/Au mask , 2006 .

[8]  Ciprian Iliescu,et al.  Characterization of masking layers for deep wet etching of glass in an improved HF/HCl solution , 2005 .

[9]  D. Aspinwall,et al.  Review on ultrasonic machining , 1998 .

[10]  Johan Roeraade,et al.  Method for fabrication of microfluidic systems in glass , 1998 .

[11]  Albert van den Berg,et al.  Powder-blasting technology as an alternative tool for microfabrication of capillary electrophoresis chips with integrated conductivity sensors , 2001 .

[12]  V. Fascio,et al.  Machining of non-conducting materials using electrochemical discharge phenomenon – An overview , 2005 .

[13]  Masayoshi Esashi,et al.  Deep reactive ion etching of Pyrex glass , 2000, Proceedings IEEE Thirteenth Annual International Conference on Micro Electro Mechanical Systems (Cat. No.00CH36308).