Synthesis of single phase i-AlCuFe bulk quasicrystal by spray forming

Abstract In the present study, an icosahedral single phase bulk quasicrystalline material based on Al62Cu25.5Fe12.5 has been synthesised by a spray forming route. Microstructural characterization showed an average grain size of 10 μm. The oversprayed fine powder showed the presence of β- and λ-phases, whereas, the deposit consited of the fully single phase bulk quasicrystalline material with compositional homogeneity. The hardness and fracture toughness measurements were carried out at different indentation loads of 50–500 g. The hardness values varied in the range 10.4–8.1 GPa and fracture toughness was seen to decrease with increasing load. The varionan of hardness with load, which is known as indentation size effect (ISE), has been established clearly. Fracture toughness value was constant in the load range from 200 to 500 g at 1.2 MPa m1/2. The cracking pattern after indentation at higher load has been observed to be intergranular as well as transgranular. The evolution of the single phase bulk quasicrystalline material has been discussed in light of the unique combination of atomization and deposition process elements in spray forming technique.

[1]  F. Turquier,et al.  Single-phase bulk Al–Cu–Fe quasicrystals by field-assisted sintering , 2008 .

[2]  F. Turquier,et al.  Synthesis of single-phase Al–Cu–Fe quasicrystals using high-energy ball-milling , 2007 .

[3]  S. Yin,et al.  Formation of Al70Cu20Fe10 icosahedral quasicrystal by mechanically alloyed method , 2007 .

[4]  R. Pérez,et al.  Morphological characteristics of the rapidly and conventionally solidified alloys of the AlCuFe system , 2007 .

[5]  P. Paufler,et al.  Micro- and nanoindentation techniques for mechanical characterisation of materials , 2006 .

[6]  J. Vuorinen,et al.  Preparation and characterisation of melt-spun Al–Cu–Fe quasicrystals , 2005 .

[7]  R. Mandal,et al.  Evolution of microstructure in spray formed Al–18%Si alloy , 2004 .

[8]  E. Huttunen-Saarivirta.  Microstructure, Fabrication and Properties of Quasicrystalline Al—Cu—Fe Alloys: A Review , 2004 .

[9]  Do hyung Kim,et al.  The toughening of Al-Cu-Fe(-B) quasicrystals by Sn particles , 2004 .

[10]  Zhou Xi-ying,et al.  Evaluation of fracture toughness of Al-Cu-Fe-B quasicrystal , 2003 .

[11]  B. Murty,et al.  Mechanical alloying of Al–Cu–Fe elemental powders , 2001 .

[12]  W. Kim,et al.  Solidification sequence of the icosahedral quasicrystal forming Al–Cu–Fe alloys , 2001 .

[13]  E. Fleury,et al.  Metal matrix composites reinforced by gas-atomised Al-Cu-Fe powders , 2000 .

[14]  E. Fleury,et al.  Effects of air plasma spraying parameters on the Al-Cu-Fe quasicrystalline coating layer , 2000 .

[15]  J. Rabier,et al.  Microindentation of Al-Cu-Fe icosahedral quasicrystal , 1999 .

[16]  J. Schroers,et al.  Dependence of phase selection and micro structure of quasicrystal-forming Al-Cu-Fe alloys on the processing and solidification conditions , 1997 .

[17]  W. Liu,et al.  Mechanical properties of quasicrystalline and crystalline phases in AlCuFe alloys , 1993 .