Accelerator adsorption onto carbon nanotubes surface affects the vulcanization process of styrene–butadiene rubber composites

The multiwalled carbon nanotubes (MWCNT) filled styrene–butadiene rubber (SBR) composites were prepared by incorporating MWCNT in a SBR/toluene solution and subsequently evaporating the solvent. These composites have shown a significant improvement in Young's modulus and tensile strength with respect to SBR gum without sacrificing high elongation at break. However, this improvement is less than expected at the higher filler content. Then, the influence of low concentrations of MWCNT on the vulcanization process of the SBR composites was studied by means of rheometer torque curves, swelling measurements, differential scanning calorimeter (DSC) analysis, and Fourier transform infrared (FTIR) spectroscopy. Also, their thermal degradation was studied by thermogravimetric analysis (TGA). It has been noticed that MWCNT affects the cure kinetics of SBR gum matrix reducing all parameters, i.e., the total heat rate and order of the reaction, scorch delay, maximum torque, and crosslink density. This effect increases as MWCNT content does, and it was attributed to the adsorption of the accelerator employed in the vulcanization (N-tert-butyl-benzothiazole-2-sulfenamide) onto the MWCNT surface. © 2009 Wiley Periodicals, Inc. J Appl Polym Sci, 2009

[1]  A. Salazar,et al.  Carboxylation treatment of multiwalled carbon nanotubes monitored by infrared and ultraviolet spectroscopies and scanning probe microscopy , 2007 .

[2]  M. Gradwell,et al.  The interaction of sulfenamide accelerators with sulfur, ZnO, and stearic acid in the absence of rubber , 1994 .

[3]  V. Singh,et al.  FTIR, Raman spectra and ab initio calculations of 2-mercaptobenzothiazole. , 2006, Spectrochimica acta. Part A, Molecular and biomolecular spectroscopy.

[4]  Agurtzane Mugica,et al.  Pyrolysis-FTIR and TGA techniques as tools in the characterization of blends of natural rubber and SBR , 2006 .

[5]  A. Wutzler,et al.  Structure and density of crosslinks in natural-rubber vulcanizates. A combined analysis by NMR spectroscopy, mechanical measurements, and rubber-elastic theory , 1992 .

[6]  Jean-Christophe Charlier,et al.  Ab initio study of benzene adsorption on carbon nanotubes , 2005 .

[7]  K. Jacob,et al.  Natural rubber nanocomposites with SiC nanoparticles and carbon nanotubes , 2006 .

[8]  A. Isayev,et al.  Injection Molding of Rubber Compounds: Experimentation and Simulation , 1991 .

[9]  K. Preston,et al.  Radical Reactions of C60 , 1991, Science.

[10]  H. Sakai,et al.  Evaluation of molecular structure in Langmuir monolayers of zinc stearate and zinc 12-hydroxystearate by IR external reflection spectroscopy , 2002 .

[11]  A. Marzocca,et al.  Carbon nanotubes as reinforcement of styrene–butadiene rubber , 2007 .

[12]  T. Kashiwagi,et al.  Flammability properties of polymer nanocomposites with single-walled carbon nanotubes: effects of nanotube dispersion and concentration * , 2005 .

[13]  A. I. Leonov,et al.  A Kinetic-Model for Sulfur Accelerated Vulcanization of a Natural-Rubber Compound , 1996 .

[14]  P. Flory,et al.  STATISTICAL MECHANICS OF CROSS-LINKED POLYMER NETWORKS II. SWELLING , 1943 .

[15]  F. Ahmadun,et al.  Multi‐Wall Carbon Nanotubes/Styrene Butadiene Rubber (SBR) Nanocomposite , 2007 .

[16]  P. Flory,et al.  Statistical Mechanics of Cross‐Linked Polymer Networks I. Rubberlike Elasticity , 1943 .

[17]  W. Xu,et al.  Polyurethane/carbon black composites with high positive temperature coefficient and low critical transformation temperature , 2005 .

[18]  M. Porter.  Structural Characterization of Filled Vulcanizates Part 1. Determination of the Concentration of Chemical Crosslinks in Natural Rubber Vulcanizates Containing High Abrasion Furnace Black , 1967 .

[19]  Q. Gong,et al.  Preparation and properties of the powder SBR composites filled with CNTs by spray drying process , 2006 .

[20]  A. Marzocca,et al.  Analysis of network structure formed in styrene–butadiene rubber cured with sulfur/TBBS system , 2007 .

[21]  A. Marzocca,et al.  An analysis of the influence of the accelerator/sulfur ratio in the cure reaction and the uniaxial stress‐strain behavior of SBR , 2004 .

[22]  T. Chuah,et al.  Effect of multi-wall carbon nanotubes on the mechanical properties of natural rubber , 2006 .

[23]  S. Shield,et al.  Use of mid‐ and near‐infrared techniques as tools for characterizing blends of copolymers of styrene–butadiene and acrylonitrile–butadiene , 2003 .

[24]  I. Szleifer,et al.  Polymers and carbon nanotubes : dimensionality, interactions and nanotechnology , 2005 .

[25]  Ivana Fenoglio,et al.  Reactivity of carbon nanotubes: free radical generation or scavenging activity? , 2006, Free radical biology & medicine.

[26]  Ji Liang,et al.  Preparation and properties of powder styrene-butadiene rubber composites filled with carbon black and carbon nanotubes , 2007 .

[27]  Y. Tanaka.  INFRARED ABSORPTION SPECTRA OF ORGANIC SULFUR COMPOUNDS. I. STUDIES ON S-N STRETCHING BANDS OF BENZENESULFONAMIDE DERIVATIVES. , 1965, Chemical & pharmaceutical bulletin.

[28]  U. Ishiaku,et al.  The effect of accelerator/sulphur ratio on the scorch time of epoxidized natural rubber , 1998 .

[29]  Shaik Jeelani,et al.  Experimental study on the thermal and mechanical properties of multi-walled carbon nanotube-reinforced epoxy , 2007 .

[30]  H. Wagner,et al.  Mechanical properties of carbon nanoparticle-reinforced elastomers , 2003 .

[31]  Zeng-min Shen,et al.  Study on preparation and properties of carbon nanotubes/rubber composites , 2006 .

[32]  A. Coran.  Chemistry of the vulcanization and protection of elastomers: A review of the achievements , 2003 .

[33]  S. Gunasekaran,et al.  FTIR spectra and mechanical strength analysis of some selected rubber derivatives. , 2007, Spectrochimica acta. Part A, Molecular and biomolecular spectroscopy.

[34]  Musa R. Kamal,et al.  Kinetics and thermal characterization of thermoset cure , 1973 .