Production of aligned helical polymer nanofibers by electrospinning

Abstract A new and simple electrospinning method has been developed for producing aligned helical polymer nanofibers. Aligned helical polycaprolactone (PCL) nanofibers were prepared by this method. The helical fibers were collected by a tilted glass slide. The morphology and loop diameters of the helical structures are dependant on the PCL solution concentration and the loop diameters are in the range of 6.9–14.9 μm for the concentration range of 4.7%–10%. The three-dimensional helical structures were obtained at the high solution concentration of 10%. These helical structures were formed by jet buckling due to mechanical instability when hitting collector surface. Formation of the helical structures is dependent on the obliquity of the tilted glass slide and distance away from the syringe needle. The converging electrical field generated by a tip collector plays an important role in the alignment of the helical structures.

[1]  Darrell H. Reneker,et al.  Bending instability of electrically charged liquid jets of polymer solutions in electrospinning , 2000 .

[2]  Martin Möller,et al.  Electrospinning with dual collection rings , 2005 .

[3]  V. Subramanian,et al.  Electrospinning of continuous aligned polymer fibers , 2004 .

[4]  R. Farris,et al.  Fabrication of aligned and molecularly oriented electrospun polyacrylonitrile nanofibers and the mechanical behavior of their twisted yarns , 2004 .

[5]  Jie Yu,et al.  Electrospinning highly aligned long polymer nanofibers on large scale by using a tip collector , 2007 .

[6]  Andreas Greiner,et al.  Electrospun nanofibers: Internal structure and intrinsic orientation , 2003 .

[7]  Darrell H. Reneker,et al.  Beaded nanofibers formed during electrospinning , 1999 .

[8]  L. Dai,et al.  Large-scale synthesis of perpendicularly aligned helical carbon nanotubes. , 2004, Journal of the American Chemical Society.

[9]  Eyal Zussman,et al.  Electrostatic field-assisted alignment of electrospun nanofibres , 2001 .

[10]  Yi Xin,et al.  Controlling poly(p-phenylene vinylene)/poly(vinyl pyrrolidone) composite nanofibers in different morphologies by electrospinning , 2006 .

[11]  Ce Wang,et al.  Influence of solvents on the formation of ultrathin uniform poly(vinyl pyrrolidone) nanofibers with electrospinning , 2004 .

[12]  Hongxia Wang,et al.  Self‐Crimping Bicomponent Nanofibers Electrospun from Polyacrylonitrile and Elastomeric Polyurethane , 2005 .

[13]  George G. Chase,et al.  Continuous Electrospinning of Aligned Polymer Nanofibers onto a Wire Drum Collector , 2004 .

[14]  W. Eccleston,et al.  Mater. Res. Soc. Symp. Proc. , 2006 .

[15]  James K. Hirvonen,et al.  Controlled deposition of electrospun poly(ethylene oxide) fibers , 2001 .

[16]  R. Kessick,et al.  Microscale polymeric helical structures produced by electrospinning , 2004 .

[17]  Min Kyoon Shin,et al.  Controlled assembly of polymer nanofibers: From helical springs to fully extended , 2006 .

[18]  Liwei Lin,et al.  Near-field electrospinning. , 2006, Nano letters.

[19]  Younan Xia,et al.  Electrospinning of polymeric and ceramic nanofibers as uniaxially aligned arrays , 2003 .

[20]  Zhong Lin Wang,et al.  Spontaneous Polarization-Induced Nanohelixes, Nanosprings, and Nanorings of Piezoelectric Nanobelts , 2003 .

[21]  Hai‐feng Zhang,et al.  Synthesis, Characterization, and Manipulation of Helical SiO2 Nanosprings , 2003 .